Preparation of graphene oxide/recycled cement-based composite materials

被引：0

作者：

Gui C. ^{[1
]}

Xu Z. ^{[1
]}

Jiang Y. ^{[1
]}

Li S. ^{[1
]}

机构：

[1] School of Material Science and Engineering, Anhui University of Science and Technology, Huainan

来源：

Fuhe Cailiao Xuebao/Acta Materiae Compositae Sinica | 2021年 / 38卷 / 05期

关键词：

Aggregates recycling; Cement hydration; Cement-based composites; Graphene oxide; Microstructure;

D O I：

10.13801/j.cnki.fhclxb.20201106.001

中图分类号：

学科分类号：

摘要：

Based on the replacement of natural sand by recycled fine aggregate from construction waste, the comprehensive physical properties and hydration mechanism of graphene oxide (GO) modified recycled cement-based composites were studied. The recycled cement-based composites were prepared by ultrasonic dispersion GO and vibration stirring. The comprehensive durability test results show that compared with recycled cement-based materials without GO, the flexural and compressive strength of the GO/recycled cement-based composites modified with 0.03% GO at 7 d age increase by 16% and 21%, respectively. The flexural strength and compressive strength of GO/recycled cement-based composites modified by 0.02% GO at 28 d age increase by 13.7% and 13.6%, respectively. The GO/recycled cement-based composite has a 7 d weather resistance and good mechanical properties after 50 freeze-thaw cycles; the chloride ion content is less than 0.06%. The radioactivity test results show that internal exposure index IRa and external exposure index Ir of GO/recycled cement-based composites belong to Class A building materials. The hydration mechanism of the GO/recycled cement-based composites was studied by XRD, TG-DTA, SEM and other means, the results show that GO promotes the large-scale formation of ettringite (AFt) crystals, and the presence of more free water in the gel pores, and has an inhibitory effect on the later generation of calcium hydroxide (CH), thereby improving the synthesis of GO/recycled cement-based composites physical properties. Copyright ©2021 Acta Materiae Compositae Sinica. All rights reserved.

引用

页码：1526 / 1534

页数：8

共 24 条

[1]

YI C., The study on the resource of construction waste for recycled aggregate concrete, (2014)

[2]

ZHANG X G, WANG F, YANG J H, Et al., Experim ental study on compressive strength of cement mortar with recycled light weight aggregate, Concrete, 4, pp. 129-132, (2017)

[3]

TUYAN M, MARDANI-AGHABAGLOU A, RAMYAR K., Freeze-thaw resistance, mechanical and transport properties of self-consolidating concrete incorporating coarse recycled concrete aggregate, Materials and Design, 53, pp. 983-991, (2014)

[4]

GAO C, HUANG L, YAN L B, Et al., Behavior of glass and carbon FRP tube encased recycled aggregate concrete with recycled clay brick aggregate, Composite Structures, 155, pp. 245-254, (2016)

[5]

DONG L L, CHEN W G, DENG N, Et al., A novel fabrication of graphene by chemical reaction with a green reductant, Chemical Engineering Journal, 306, pp. 754-762, (2016)

[6]

YANG H B, CUI H Z, TANG W C, Et al., A critical review on research progress of graphene/cement based composites, Composites Part A: Applied Science and Manufacturing, 102, pp. 273-296, (2017)

[7]

NIETO A, BISHT A, LAHIRI D, Et al., Graphene reinforced metal and ceramic matrix composites: A review, Metallurgical Reviews, 62, 5, pp. 241-302, (2016)

[8]

LEE C G, WEI X D, KYSAR J W, Et al., Measurement of the elastic properties and intrinsic strength of monolayer graphene, Science, 321, 5887, pp. 385-388, (2008)

[9]

LEI B, ZOU J, RAO C H, Et al., Experimental study on modification of recycled concrete with graphone oxide, Journal of Building Structures, 37, s2, pp. 103-108, (2016)

[10]

GUO K, MIAO H, ZHOU J H., Effect of graphene oxide on gas permeability of recycled concrete, Journal of Shenyang Jianzhu University (Natural Science), 35, 4, pp. 692-698, (2019)

← 1 2 3 →