Voltammetric characterization for the growth of oxide films formed on copper in air

被引：0

作者：

Nakayama, Shigeyoshi ^{[1
]}

Shibata, Masahiro ^{[1
]}

Kuwabata, Susumu ^{[2
]}

Osakai, Toshiyuki ^{[3
]}

Notoya, Takenori ^{[4
]}

机构：

[1] Analysis Technology Research Center, Sumitomo Electric Industries, Ltd., 1-1-3, Shimaya, Konohana-ku, Osaka 554-0024, Japan

[2] Department of Materials Chemistry, Graduate School of Engineering, Osaka University, 2-1, Yamada-oka, Suita 565-0871, Japan

[3] Department of Chemistry, Faculty of Science, Kobe University, 1-2-1, Tsurukabuto, Nada-ku, Kobe 657-8501, Japan

[4] Molecular Science Division, Graduate School of Engineering, Hokkaido University, 13-8, Kita, Kita-ku, Sapporo 060-8628, Japan

来源：

Zairyo to Kankyo/ Corrosion Engineering | 2002年 / 51卷 / 12期

关键词：

Copper compounds - Corrosion - Cyclic voltammetry - Electrolytes - Oxidation - Reaction kinetics;

D O I：

10.3323/jcorr1991.51.566

中图分类号：

学科分类号：

摘要：

The growth mechanisms of oxide films thermally formed on copper have been studied using double sweep cyclic voltammetry in strongly alkaline electrolytes. It was found that an electrolyte of 6M KOH + 1M LiOH allowed perfect resolution of cathodic waves due to the reduction of Cu2O and CuO. The effect of the types of anion on copper oxidation mechanism was investigated in many factors of corrosion. C opper sheets were prepared by pre immersion in various electrolytes of sodium salt, followed by heating in air at 80°C and 90% RH. The formation kinetics of each oxide films followed the parabolic rate law with a few exceptions. These were confirmed that the formation of the oxide films was accelerated with the increase of ions on copper and that the oxidation rate of Cu2O or CuO was controlled by the types of anion.

引用

页码：566 / 570

共 50 条

[31] Fabrication, Characterization and Photocatalytic Activity of Copper Oxide Nanowires Formed by Anodization of Copper Foams
Abd-Elnaiem, Alaa M.
Abdel-Rahim, Moustafa A.
Abdel-Latief, Atta Y.
Mohamed, Ahmed Abdel-Rahim
Mojsilovic, Kristina
Stepniowski, Wojciech Jerzy
MATERIALS, 2021, 14 (17)
[32] Growth of novel nanostructured copper oxide (CuO) films on copper foil
Zhang, Weixin
Ding, Shaixia
Yang, Zeheng
Liu, Anping
Qian, Yitai
Tang, Shupei
Yang, Shihe
JOURNAL OF CRYSTAL GROWTH, 2006, 291 (02) : 479 - 484
[33] THE GROWTH AND REDUCTION OF DUPLEX OXIDE-FILMS ON COPPER
SPECKMANN, HD
LOHRENGEL, MM
SCHULTZE, JW
STREHBLOW, HH
BERICHTE DER BUNSEN-GESELLSCHAFT-PHYSICAL CHEMISTRY CHEMICAL PHYSICS, 1985, 89 (04): : 392 - 402
[34] OXIDE-GROWTH ON COPPER THIN-FILMS
PAOLETTI, L
ROSA, PA
PICOZZI, P
SANTUCCI, S
ULTRAMICROSCOPY, 1984, 12 (1-2) : 116 - 116
[35] Characterization of anodic films formed on copper in 0.1 M borax solution
Ribotta, S. B.
La Morgia, L. F.
Gassa, L. M.
Folquer, M. E.
JOURNAL OF ELECTROANALYTICAL CHEMISTRY, 2008, 624 (1-2) : 262 - 268
[36] Epitaxial growth and characterization of oxide thin films
Yang, GZ
Lu, HB
Zhao, T
Chen, F
Chen, ZH
FOURTH INTERNATIONAL CONFERENCE ON THIN FILM PHYSICS AND APPLICATIONS, 2000, 4086 : 382 - 386
[37] GROWTH AND CHARACTERIZATION OF ZIRCONIUM-OXIDE FILMS
GAO, YM
WU, P
KERSHAW, R
DWIGHT, K
WOLD, A
MATERIALS RESEARCH BULLETIN, 1990, 25 (07) : 871 - 876
[38] Growth and characterization of tin oxide thin films
Fu, L
Pan, X
CERAMIC PROCESSING SCIENCE, 1998, 83 : 325 - 325
[39] ELECTRICAL-PROPERTIES OF ANTIMONY OXIDE-FILMS FORMED BY HEATING ANTIMONY FILMS IN AIR
NIKAM, PS
MANKAR, DL
INDIAN JOURNAL OF PURE & APPLIED PHYSICS, 1983, 21 (06) : 361 - 362
[40] THE OXIDE FILMS FORMED ON COPPER SINGLE CRYSTAL SURFACES IN PURE WATER .1. NATURE OF THE FILMS FORMED AT ROOM TEMPERATURE
KRUGER, J
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1959, 106 (10) : 847 - 853

← 1 2 3 4 5 →