Study on microstructure and mechanical properties of laser repaired 1Cr12Ni3MoVN alloy

被引:3
作者
Xue L. [1 ]
Lu P. [1 ]
Chen J. [1 ]
Lin X. [1 ]
Huang W. [1 ]
机构
[1] State Key Laboratory of Solidification Processing, Northwestern Polytechnical University, Xi'an
来源
Zhongguo Jiguang/Chinese Journal of Lasers | 2010年 / 37卷 / 03期
关键词
1Cr11Ni2W2MoV alloy; 1Cr12Ni3MoVN alloy; Laser repair; Laser technique; Martensite; Microstructure; Tensile properties;
D O I
10.3788/CJL20103703.0887
中图分类号
学科分类号
摘要
In the present paper, 1Cr12Ni3MoVN alloy was repaired by laser repair (LR) with 1Cr11Ni2W2MoV. A very good metallurgical bond between the repaired zone and the substrate was achieved. The microstructure of the laser repaired zone (LRZ) is composed by martensite and tempered martensite, and a quenching phenomenon was observed in heat affected zone (HAZ). Micro-hardness values decreased from LRZ to substrate zone (SZ), the maximum value happened in the HAZ close to the melting line. The results of room temperature tensile tests show that the strength of LRZ is 1280~1380 MPa, while the strength of laser repaired sample is 965~980 MPa. Fractures were observed on casting substrate during tensile test.
引用
收藏
页码:887 / 890
页数:3
相关论文
共 11 条
[1]  
Wu J., Liu J., Chen M., Development of 1Cr12Ni3MoVN(S/SJ2) forgings, Shanghai Steel & Iron Research, 4, pp. 35-41, (2006)
[2]  
Xue L., Huang W., Chen J., Et al., Application of laser forming repair technology on the aerial castings, Foundry Technology, 29, 3, pp. 391-394, (2008)
[3]  
Guo Y., Liang G., Li L., Laser cladding reparation of aluminum alloy, Chinese J. Lasers, 35, 2, pp. 303-306, (2008)
[4]  
Keicher D.M., Smugeresky J.E., Romero J.A., Et al., Using the laser engineered net shaping (LENS) process to produce complex components from a CAD solid model, 2293, pp. 91-97, (1995)
[5]  
Gaumann M., Henry S., Cleton F., Et al., Epitaxial laser metal forming: analysis of microstructure formation, Materials Science & Engineering A, A271, pp. 232-241, (1999)
[6]  
Wu X., Liang J., Mei J., Et al., Microstructures of laser-deposited Ti-6Al-4V, Materials and Design, 25, pp. 137-144, (2004)
[7]  
Zhu X., Zhong M., Liu W., Et al., Laser cladding repairing of directionally solidified Ni-base superalloy and its tensile property, Chinese J. Lasers, 34, s1, pp. 185-189, (2007)
[8]  
Wang X., Chen J., Lin X., Et al., Microstructures of laser forming repair 7050 aluminum alloy with AlSi12 powder, Chinese J. Lasers, 36, 6, pp. 1585-1590, (2009)
[9]  
Panton-Kent, Phase Balance in 9%Cr1%Mo Steel Welds, (1991)
[10]  
C-Lippold J., J-Kotecki D., Welding Metallurgy and Weldability of Stainless Steels, pp. 236-237, (2008)