Controllability research on dilution ratio of nickel-based superalloy by laser cladding reparation

被引：0

作者：

Pan, Hu ^{[1
]}

Zhao, Jianfeng ^{[1
]}

Liu, Yunlei ^{[1
]}

Wang, Kai ^{[1
]}

Xiao, Meng ^{[1
]}

Gao, Xuesong ^{[1
]}

机构：

[1] College of Mechanical and Electrical Engineering, Nanjing University of Aeronautics and Astronautics, Nanjing

来源：

Zhongguo Jiguang/Chinese Journal of Lasers | 2013年 / 40卷 / 04期

关键词：

Dilution ratio; Laser cladding reparation; Laser technique; Powder-heat-absorption density; Process parameter; Regression analysis;

D O I：

10.3788/CJL201340.0403007

中图分类号：

学科分类号：

摘要：

In order to improve the stability of laser cladding reparation property, several single-factor tests are carried out for GH4169 nickel-based superalloy by controlling the dilution ratio. The result shows that within certain parameter range, the dilution ratio increases with the increase of laser power or the decrease of feeding speed, and the scanning speed may have little influence. In order to simplify the study process of dilution ratio, this paper puts forward the concept of powder-heat-absorption density, which means the laser energy absorbed by a unit mass of powder during the process of laser cladding, establishes the positive correlation between the powder heat absorption and dilution ratio with the combination between laser power and power feeding speed. By using the regression thoughts and with the data analysis about the test results by SPSS software, the relation model between powder heat absorption and dilution ratio is established and the accuracy is verified, which provides the theoretical references and test support about the study of stability of laser cladding reparation property of nickel-based superalloy.

引用

共 20 条

[1]

Song Z., Aviation Engine Reliability and Fault Inhibition Engineering, pp. 10-11, (2002)

[2]

Xu S., Xiao Y., Li J., Organization property researches of the laser repair technology in the helicopter engine turbine oriented implement, Acta Optica Sinica, 30, 8, pp. 2311-2316, (2010)

[3]

Gaumann M., Henry S., Cleton F., Et al., Epitaxial laser metal forming: Analysis of microstructure formation, Materials Science and Engineering: A, 271, 1-2, pp. 232-241, (1999)

[4]

Cheikh H.E., Courant B., Branchu S., Et al., Analysis and prediction of single laser tracks geometrical characteristics in coaxial laser cladding process, Optics and Lasers in Engineering, 50, 3, pp. 413-422, (2012)

[5]

Zhu G., Zhang A., Li D., Effect of process parameters on surface smoothness in laser cladding, Chinese J. Lasers, 37, 1, pp. 296-301, (2010)

[6]

Chryssolouris G., Zannis S., Tsirbas K., Et al., An experimental investigation of laser cladding, CIRP Annals-Manufacturing Technology, 51, 1, pp. 145-148, (2002)

[7]

Kim J.D., Peng Y., Melt pool shape and dilution of laser cladding with wire feeding, J. Materials Processing Technology, 104, 3, pp. 284-293, (2000)

[8]

Zhang Q., Liu W., Yang S., Et al., Analysis model of dilution and related factor in process of powder feeding laser cladding, J. Iron and Steel Research, 14, 1, pp. 11-15, (2002)

[9]

Liu X., Lian J., Zhang Q., Characteristics of the bound interface between the coating and the substrate formed by powder feeding laser cladding, Chinese J. Mechanical Engineering, 37, 4, pp. 38-43, (2001)

[10]

Ge J., Zhang A., Li D., Et al., Process research on DZ125L superalloy parts by laser metal direct forming, Chinese J. Lasers, 38, 7, (2011)

← 1 2 →