Mechanical Properties Of Hybrid Woven Carbon/E-Glass/Polypropylene Thermoplastic Prepreg Composites

An increased request in composite materials at low prices with high specific properties has contributed to the development of hybrid thermoplastic composites. In this study, intra-ply, inter-ply and intra-ply/inter-ply hybrid thermoplastic composites are developed by using hybrid woven Carbon/Polypropylene (PP), E-glass/PP and Carbon/E-glass/PP prepregs and their behaviors under axial loading are compared with non-hybrid composites. The intra-ply/inter-ply hybrid composites, which have equable and uniform fiber placement/fiber fractions, provide the highest tensile strength and modulus values. The intra-ply/inter-ply hybrid composite in which the delamination is limited to a narrow region provides high tensile strength/modulus values and therefore this composite is considered as damage tolerant material. © 2012 Journal of Textiles and Engineer.; Kompozit malzemelerde yüksek spesifik özelliklere düsük fiyatlarda ulasma isteginin çesitli endüstriyel uygulama alanlari için giderek artmasi, hibrit termoplastik kompozitlerin gelistirilmesine katkisaglamistir. Bu çalismada, hibrit dokunan Karbon/Polipropilen (PP), E-cam/PP ve Karbon/E-cam/PP prepregler kullanilarak, katman-içi, katmanlar-arasive katmaniçi/katmanlar-arasihibrit biçimde tasarlanan termoplastik kompozitler gelistirilmisve bu kompozitlerin eksenel yüke maruz kalmasi durumundaki davranislarihibrit-olmayan kompozitlerle karsilastirilmistir. Hibritlemede kullanilan takviye liflerinin konum ve lif miktaribakimindan dengeli/uniform dagilima sahip oldugu katman-içi/katmanlar-arasihibrit kompozit yapien yüksek dayanim/modül degerini göstermistir. Katman-içi/katmanlar-arasihibrit kompozit yapi, gerek daha dar bir alanda sinirlanan delaminasyon davranisi, gerekse yüksek çekme dayanim/modül degerleri bakimindan hasar toleranslimalzeme olarak degerlendirilmistir. © 2012 Journal of Textiles and Engineer.