Superior Piezoelectric Performance in Textured CaBi2Nb2O9 Ferroelectric Ceramics through Rare-Earth Gadolinium Doping and Spark Plasma Sintering

High-performance piezoelectric ceramics with excellent thermal stability are crucial for high-temperature piezoelectric sensor applications. However, conventional fabrication processes offer limited enhancements in piezoelectric performance. In this study, we achieved a significant breakthrough in the piezoelectric performance of highly textured CaBi2Nb2O9 (CBN) ceramics by incorporating rare-earth gadolinium doping and utilizing spark plasma sintering. The resulting Ca0.97Gd0.03Bi2Nb2O9 (CBN-3Gd) ceramics exhibited superior piezoelectric properties, with a high piezoelectric constant d(33) of 26 pC/N and a high Curie temperature T-C of 946 degrees C. We employed piezoresponse force microscopy (PFM) to observe the morphology and dimensions of the ferroelectric domains, revealing a rod-shaped 3D domain configuration. This configuration facilitated polarization rotation in the textured ceramics, as analyzed using X-ray photoelectron spectroscopy (XPS) and polarization-electric field (P-E) hysteresis loops. Furthermore, the textured CBN-3Gd ceramics demonstrated exceptional thermal stability and reliability. The piezoelectric constant d(33) decreased by only 11.8% over a temperature range of room temperature to 500 degrees C, and the DC electrical resistivity remained at 6.7 x 10(5) Omega cm at 600 degrees C. This work not only highlights the great potential of textured CBN-based ceramics for high-temperature piezoelectric sensors but also provides a viable strategy for enhancing the performance of piezoelectric materials with large aspect ratio micromorphology.