Preparation of Phosphorus-Nitrogen Flame Retardant PiP-DOPO and Its Flame Retarded Epoxy Resin

被引：0
|
作者：
Wang Z. [1 ]
Liang B. [1 ]
Liu X. [1 ]
机构：
[1] School of Materials Science and Engineering, Shenyang University of Chemical Technology, Shenyang
来源：
Gaofenzi Cailiao Kexue Yu Gongcheng/Polymeric Materials Science and Engineering | 2018年 / 34卷 / 08期
关键词：
Composites; Epoxy resin; Flame retardance; Phosphorus nitrogen flame retardant; Thermal properties;
D O I：
10.16865/j.cnki.1000-7555.2018.08.025
中图分类号：
学科分类号：
摘要：
The phosphorus-nitrogen flame retardant 6, 6'- (piperazine-1, 4-diyl) bis (6H-dibenzo [c, e][1, 2] oxophosphate-6-oxide)PiP-DOPO was synthesized using piperazine, 9, 10-2H-9-oxa-10-phospaphenanthrene-10-oxide (DOPO) and carbon tetrachloride as raw materials. Its structure was characterized by FT-IR and 1H-NMR, and PiP-DOPO was used to flame retarded epoxy resin (EP). The thermal properties of PiP-DOPO and cured products were investigated by TGA, flame retardant properties were characterized by limit oxygen index (LOI), vertical burning test (UL 94) and cone calorimeter test (CCT), and the residual carbon morphology was investigated by SEM. The results show that when the phosphorus content is 1.50% in the EP system, the carbon residue rate could reach 25.23% from 23.02% (pure EP) at 600 ℃ (in N2 atmosphere), the LOI reaches 27.5, the UL 94 passes V-0 level, the PHRR is 325.0 kW/m2, THR is 76.8 MJ/m2. And the SEM result reveals that the addition of PiP-DOPO can obviously improve the carbon residue morphology after combustion. So, the PiP-DOPO can enhance the flame retardant properties of epoxy resin. © 2018, Editorial Board of Polymer Materials Science & Engineering. All right reserved.
引用
收藏
页码：149 / 153and160
相关论文
共 18 条
  • [1] Jiao C.M., Dong J., Zhang C.J., Et al., Synthesis and properties of a phosphate ester as curing agent in an epoxy resin system, Iran Polym. J., 23, pp. 591-598, (2014)
  • [2] Ma S.Q., Liu X.Q., Jiang Y.H., Et al., Synthesis and properties of phosphorus-containing bio-based epoxy resin from itaconicacid, Sci. China Chem., 57, pp. 379-388, (2014)
  • [3] Liang B., Wang G., Hong X.D., Et al., Synthesis and properties of a new halogen-free flame-retardant epoxy resin curing agent, High Perform. Polym., 28, pp. 110-118, (2016)
  • [4] Han M.X., Xu M.J., Li B., Synthesis and flame retardant properties of a novel phosphorous-containing flame retardant DOPO-PPO, Chinese Journal of Synthetic Chemistry, 24, 2, pp. 98-101, (2016)
  • [5] Peng S.P., Tao C.C., Lu X., Et al., Study on synthesis and flame retardancy of new nitrogen-containing flame retardant, China Plastics Industry, 36, 5, pp. 67-69, (2008)
  • [6] Shan J.L., Song R.J., Li B., Study on preparation of a novel silicon-containing flame retardant and its application in polycarbonate, Plastics Science and Technology, 44, 4, pp. 90-94, (2016)
  • [7] Li Z.S., Liu J.G., Et al., Thermal and combustion behavior of phosphorus-nitrogen and phosphorus-silicon retarded epoxy, Iran Polym. J., 26, pp. 21-30, (2017)
  • [8] Xiong Y.Q., Jiang Z.J., Xie Y.Y., Et al., Development of a DOPO-containing melamine epoxy hardeners and its thermal and flame-retardant properties of cured products, J. Appl. Polym. Sci., 127, pp. 4352-4358, (2013)
  • [9] Wirasaputra A., Yao X.H., Zhu Y.M., Et al., Flame-retarded epoxy resins with a curing agent of DOPO-triazine based anhydride, Macromol. Mater. Eng., 301, pp. 982-991, (2016)
  • [10] Wang P., Cai Z.S., Highly efficient flame-retardant epoxy resin with a novel DOPO-based triazole compound: Thermal stability, flame retardancy and mechanism, Polym.Degrad.Stab., 137, (2017)
12