Tensile properties of L12 intermetallic foils fabricated by cold rolling

被引：19

作者：

Kaneno, Yasuyuki ^{[1
]}

Myoki, Tadamichi ^{[1
]}

Takasugi, Takayuki ^{[1
]}

机构：

[1] Department of Materials Science, Osaka Prefecture University, 1-1 Gakuen-cho, Naka-ku, Sakai, Osaka,599-8531, Japan

来源：

| 2008年 / Carl Hanser Verlag卷 / 99期

关键词：

Nickel compounds - Annealing - Binary alloys - Silicon alloys - Temperature - Fracture - Tensile strength - Cobalt alloys - Polycrystalline materials - Aluminum alloys - Cold rolling - Metal cladding - High strength alloys - Intermetallics - Titanium alloys;

D O I：

10.3139/146.101757

中图分类号：

学科分类号：

摘要：

Polycrystalline L12 -type Ni3(Si,Ti), Ni3Al and Co3Ti alloys prepared through thermomechanical processing from arcmelted ingots were successfully cold-rolled to thin foils with a thickness of less than 200 lm. The cold-rolling with over 90% reduction in thickness was possible without providing intermediate annealing. The cold-rolled foils showed high tensile strength (2 GPa) at room temperature although no plastic elongation was observed. The tensile strength of the annealed foils generally decreased acquiring a certain level of fracture strain. Room temperature fracture strain increased with increasing annealing temperature, and reached to 30-40%by a high temperature annealing at 1173 K. Among three kinds of intermetallic alloys, the Ni3(Si, Ti) foil annealed around at 900 K exhibited an extremely high tensile strength and yield strength (over 2 GPa) with a reasonable fracture strain. Also, it was found that the fully-recrystallized Ni3(Si, Ti) and Co3Ti foils showed a strength anomaly at intermediate testing temperature. The observed tensile properties, especially tensile strength at low temperature as well as at high temperature for the present L12 intermetallic foils, were found to be superior to those for the conventional alloys such as nickel based alloys and stainless steels.