Preparation and properties of Cu-doped SnO2/TiO2 film

被引:0
作者
Wang, Guo-Dong [1 ]
Wei, Chang-Ping [1 ]
He, Rui-Ying [1 ]
San, Jing [1 ]
Peng, Chun-Jia [1 ]
机构
[1] School of Chemistry and Environmental Engineering, Changchun University of Science and Technology, Changchun
来源
Faguang Xuebao/Chinese Journal of Luminescence | 2015年 / 36卷 / 09期
关键词
Cu-doping; Photocatalysis; SnO[!sub]2[!/sub]/TiO[!sub]2[!/sub] film; Sol-gel method;
D O I
10.3788/fgxb20153609.0996
中图分类号
学科分类号
摘要
Cu-doped nano-SnO2TiO2 gelatins were prepared and coated onto glass substrates by spin coating method, followed by drying at low temperature and calcined at high temperature. The films were characterized by XRD, SEM, EDS, and UV-Vis. The photocatalysis degradation efficiency was studied by using methyl orange as probe. XRD patterns show that the films are anatase structure. SEM images show that the surfaces of the films are flat without obvious crack, and the average diameter is about 20 nm. EDS results indicate that Cu has been introduced to SnO2/TiO2 films. UV-Vis absorption spectra show that the absorbance of Cu-doped SnO2/TiO2 films at visible region increase comparing to pure TiO2 film. The degradation experiment under UV light shows that the photocatalysis degradation efficiency of Cu-doped SnO2/TiO2 film is higher than that of pure TiO2 film. The photocatalysis degradation efficiency is the biggest when the doping mole fraction of Cu is 10%. ©, 2015, Chines Academy of Sciences. All right reserved.
引用
收藏
页码:996 / 1000
页数:4
相关论文
共 17 条
[1]  
Shang J., Xie S.D., Liu J.G., Progress in SnO<sub>2</sub>/TiO<sub>2</sub> composite semiconductor nanofilm, Prog. Chem., 17, 6, pp. 1012-1023, (2005)
[2]  
Cai Z.Q., Low-temperature Preparation and Properties of TiO<sub>2</sub>/SnO<sub>2</sub> Composite Sols and Composite Films, (2007)
[3]  
Cai Z.Q., Shen Q.H., Gao J.W., Et al., Studies of the photocatalytic activity of the TiO<sub>2</sub>/SnO<sub>2</sub> composite films, J. Ceram., 27, 3, pp. 281-282, (2006)
[4]  
Xu Q.C., Diana V.W., Rose A., Et al., Superhydrophilicity-assisted preparation of transparent and visible light activated N-dopedtitania film, Nanoscale, 2, pp. 1122-1127, (2010)
[5]  
Li J.C., Wang B.F., Shan L.T., Et al., Growth and characterization of sol-gel CuO-doped SnO<sub>2</sub> films, Chin. J. Vaccum. Sci. Technol., 32, 3, pp. 225-227, (2012)
[6]  
Trapalis C., Kozhukharov V., Samuneva B., Et al., Sol-gel processing of titanium-containing thin coatings, J. Mater. Sci., 28, 5, pp. 1276-1282, (1993)
[7]  
Kristopher P., Robert G.P., Ivan P.P., Et al., Titania and silver-titania composite films on glass-Potent antimicrobial coatings., J. Mater. Chem., 17, 1, pp. 95-104, (2007)
[8]  
Andrew M., Nicholas E., George H., Et al., Preparation and characterisation of novel thick sol-gel titania film photocatalysts, Photochem. Photobiol. Sci., 2, pp. 591-596, (2003)
[9]  
Tai W.P., Inoue K., Oha J.H., Ruthenium dye-sensitized SnO<sub>2</sub>/TiO<sub>2</sub> coupled solar cells, Sol. Energy Mater. Sol. Cells, 71, 4, pp. 553-557, (2002)
[10]  
Duan J.Y., Li F.Q., Wang J., Preparation of sol by sol-gel method, J. Hebei Univ. Eng., 28, 1, pp. 57-58, (2011)