Effects of dipping temperature on hot-dip Galfan coating of steel wire

被引：0
|
作者：
Du, An [1 ]
Ma, Rui-Na [1 ]
Fan, Yong-Zhe [1 ]
Cao, Xiao-Ming [1 ]
Shi, Jian [1 ]
Wang, Feng-Hua [1 ]
机构：
[1] Material Science and Engineering Institute, Hebei University of Technology, Tianjin 300130, China
来源：
Cailiao Rechuli Xuebao/Transactions of Materials and Heat Treatment | 2010年 / 31卷 / 11期
关键词：
Compendex;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Aluminum oxide
引用
收藏
页码：144 / 148
相关论文
共 5 条
  • [1] Microstructure and performance of hot-dip aluminizing coating of copper
    School of Mechanical Engineering, University of Shanghai for Science and Technology, Shanghai
    200093, China
    不详
    200093, China
    Xiyou Jinshu, 10 (955-960):
  • [2] NEW DEVELOPMENTS IN CONTINUOUS HOT-DIP ZINC COATING OF COLD-ROLLED STEEL SHEET.
    Anon
    Industrial Heating, 1980, 47 (09): : 24 - 26
  • [3] Non-destructive corrosion diagnosis of painted hot-dip galvanizing steel sheets by using THz spectral imaging
    Nakamura, Yuta
    Kariya, Hidetaka
    Sato, Akihiro
    Tanabe, Tadao
    Nishihara, Katsuhiro
    Taniyama, Akira
    Nakajima, Kaori
    Maeda, Kensaku
    Oyama, Yutaka
    Zairyo to Kankyo/ Corrosion Engineering, 2014, 63 (09): : 504 - 509
  • [4] Influences of Zinc Coating Structure on the Drawing Result during Wet Drawing of Hot Dip Galvanized Thin High-Strength Steel Wires.
    Apel, Geunther
    Nuenninghoff, Rolf
    1979, 99 (25-26): : 1482 - 1486
  • [5] Role of TiAl3 fine precipitate in nucleation of the primary Al dendrite phase during solidification in hot-dip Zn-11%Al-3%Mg-0.2%Si coated steel sheet
    Kimitsu RandD Lab, Technical Development Bureau, Nippon Steel Corp., Kimitsu 299-1141, Japan
    不详
    不详
    Mater. Trans., 1 (90-95):
1