Interaction of CLAM steel with plasma in HT-7 tokamak during high parameter operation

被引：7

作者：

Li, Chunjing ^{[1
]}

Huang, Qunying ^{[1
]}

Feng, Yan ^{[1
]}

Li, Jiangang ^{[1
]}

Kong, Mingguang ^{[2
]}

机构：

[1] Institute of Plasma Physics, Chinese Academy of Sciences

[2] Institute of Solid State Physics, Chinese Academy of Sciences

来源：

Plasma Science and Technology | 2007年 / 9卷 / 04期

关键词：

CLAM; PFM; PSI;

D O I：

10.1088/1009-0630/9/4/22

中图分类号：

学科分类号：

摘要：

A Plasma Surface Interaction (PSI) experiment on China Low Activation Martensitic (CLAM) steel was done to check if CLAM steel could be used as a Plasma Facing Material (PFM). A specimen with a diameter of 45 mm was exposed to 897 shots of deuterium plasmas with a total duration of 712 sec at a minor radius of 30 cm in HT-7 tokamak. During the exposure experiment, no observable influence was found on plasma performance. After exposure, the surface of the specimen seemed as smooth as before but with some colour change at the margin of the specimen. Even though some micro-damage, such as dense blisters, melting, splashing, depositions, and dust, was found on local surfaces with Scanning Electron Microscopic (SEM) observation. The reflectivity of the specimen decreased only slightly. All of these shows CLAM steel has good stability and irradiation resistance. With further optimization, it could possibly be used as the first mirror material for plasma diagnostics in tokamaks.

引用

页码：484 / 487

页数：3

共 14 条

[1]

Wu C.H., Alessandrini C., Bonal J.P., Et al., Fusion Eng. & Des., 56-57, (2001)

[2]

Krieger K., Geier A., Gong X., Et al., J. Nucl. Mater., 313-316, (2003)

[3]

Muroga T., Gasparotto M., Zinkle S.J., Et al., Fusion Eng. & Des., 61-62, (2002)

[4]

Wu Y., Qian J.P., Yu J.N., J. Nucl. Mater., 307-311, (2002)

[5]

Wu Y., Team F., Fusion Eng. & Des., 81, 23-24, (2006)

[6]

Tsuzuki K., Shinohara K., Kamiya K., Et al., J. Nucl. Mater., 329-333, (2004)

[7]

Tsuzuki K., Sato M., Kawashima H., Et al., J. Nucl. Mater., 307-311, (2002)

[8]

Qunying H., Jinnan Y., Farong W., Et al., J. Nucl. Sci. & Eng., 24, (2004)

[9]

Wu Y., Fds Team., Design concept and testing strategy of a dual functional lithium lead test blanket module for ITER and EAST., Nucl. Fusion, (2006)

[10]

Wu Y., Fds Team., Design and analysis of the Chinese dual-functional lithium lead(DFLL) test blanket module for ITER., Fusion Eng. & Des., (2006)

← 1 2 →