Fracture toughness of CGHAZ of Q690CFD high-strength steel

被引：0

作者：

Zhang N. ^{[1
,2
]}

Tian Z. ^{[2
]}

Zhang X. ^{[1
]}

Yang J. ^{[1
]}

机构：

[1] Shougang Research Institute of Technology, Beijing

[2] Central Iron & Steel Research Institute, Beijing

来源：

Hanjie Xuebao/Transactions of the China Welding Institution | 2018年 / 39卷 / 01期

关键词：

CGHAZ; CTOD; High angle boundary; M/A; Welding;

D O I：

10.12073/j.hjxb.2018390007

中图分类号：

学科分类号：

摘要：

The coarse grain heat affect zone (CGHAZ) of Q690CFD high-strength steel with two different compositions was simulated with Gleeble-1500 test machine to investigate its impact toughness, and the values of CTOD were measured by a series of three point bending tests. The fracture behavior of crack tip in CGHAZ was analyzed based on the fractography of CTOD samples with SEM. The results show that the variation trend of fracture toughness (critical CTOD values δ m/c/u(8) and instrumented extension energy) declined with the decrease of temperature. The ductile-brittle transition temperature, fitted by Boltzmann function, was accordant with the variation tendency of instrumented impact. The path of crack propagation in CGHAZ of two different Q690CFD steels was determined by the position of high angle boundaries (≥15°) and M/A islands in metastructure nearby the fracture zone. © 2018, Editorial Board of Transactions of the China Welding Institution, Magazine Agency Welding. All right reserved.

引用

页码：26 / 31and36

页数：3110

共 5 条

[1]

Yang X., Wang D., Li X., Et al., Large-sized CTOD test for welded joints of offshore petroleum plat-form, Transactions of the China Welding Institution, 23, 4, pp. 48-52, (2002)

[2]

Wu Y.M., Wang Y.Q., Shi Y.J., Effects of low temperature on properties of structural steels, Journal of University of Science and Technology, 11, 5, pp. 442-446, (2004)

[3]

Zhang X., Dong X., Chen Y., Et al., Study on reheat embitterment in coarse-grain region of heat affected zone (CGHAZ) of Q690CFD, Iron and Steal, 45, 11, (2010)

[4]

Wang Y., Liu X., Shi Y., The fracture toughness of butt weld at low temperature of 960 MPa high-structure steel, Chinese Journal of Materials Research, 27, 3, pp. 238-246, (2013)

[5]

Wang Y., Zhou H., Xi W., Et al., Experimental study on mechanical properties of thermit joints of rail steels at low temperature, Transactions of the China Welding Institution, 31, 7, pp. 13-16, (2010)

← 1 →