Microstructure of hydroxyapatite/collagen coating on AZ31 magnesium alloy by a solution treatment

被引：8

作者：

Bao Q. ^{[1
]}

Zhao L. ^{[1
]}

Jing H. ^{[1
]}

Xu Q. ^{[1
]}

机构：

[1] School of Materials Science and Engineering, Anhui University of Technology, Anhui Maanshan

来源：

Journal of Biomimetics, Biomaterials and Biomedical Engineering | 2017年 / 30卷

关键词：

Coating; Collagen; Hydroxyapatite; Magnesium;

D O I：

10.4028/www.scientific.net/JBBBE.30.38

中图分类号：

学科分类号：

摘要：

HA and HA/Col coatings were prepared by a solution treatment on AZ31 magnesium alloy. The microstructure and composition of coatings were studied by SEM, XRD. In vitro study was performed by immersion the sample In Hank's solution for 7 days. The H2 evolution of the HA/Col coating was as low as 0.24 ml/cm2 which can insignificant increase the corrosion resistance of AZ31. © 2017 Trans Tech Publications Ltd, Switzerland.

引用

页码：38 / 44

页数：6

共 20 条

[1]

Song Y., Shan D., Chen R., Zhang F., Han E.-H., Formation mechanism of phosphate conversion film on Mg-8.8Li alloy, Corros Sci, 51, 2009, pp. 62-69

[2]

Bao Q.H., Li X.X., Zhang C., Sun C., Preparation and Characterization of DPCD Coating on Mg-Ca-Zn Magnesium Alloy by a Phosphating Treatment, Thrombosis and Haemostasis, 20, pp. 65-71, (2014)

[3]

Tomozawa M., Hiromoto S., Microstructure of hydroxyapatite- and octacalcium phosphate-coatings formed on magnesium by a hydrothermal treatment at various pH values, Acta Mater, 59, pp. 355-363, (2011)

[4]

Geng F., Tan L.L., Jin X.X., Yang J.Y., Yang K., The preparation, cytocompatibility, and in vitro biodegradation study of pure β-TCP on magnesium, Journal of Materials Science Materials in Medicine, 20, 2009, pp. 1149-1157

[5]

Tomozawa M., Hiromoto S., Harada Y., Microstructure of hydroxyapatite-coated magnesium prepared in aqueous solution, Surface and Coatings Technology, 204, pp. 3243-3247, (2010)

[6]

Chen X.B., Birbilis N., Abbott T.B., A simple route towards a hydroxyapatite-Mg (OH) 2 conversion coating for magnesium, Corros Sci, 53, pp. 2263-2268, (2011)

[7]

Bakhsheshi-Rad H.R., Hamzah E., Daroonparvar M., Yajid M.A.M., Medraj M., Fabrication and corrosion behavior of Si/HA nano-composite coatings on biodegradable Mg-Zn-Mn-Ca alloy, Surface and Coatings Technology, 258, pp. 1090-1099, (2014)

[8]

Tomozawa M., Hiromoto S., Growth mechanism of hydroxyapatite-coatings formed on pure magnesium and corrosion behavior of the coated magnesium, Appl Surf Sci, 257, pp. 8253-8257, (2011)

[9]

Temizel N., Girisken G., Tas A.C., Accelerated transformation of brushite to octacalcium phosphate in new biomineralization media between 36.5°C and 80°C, Materials Science and Engineering: C, 31, pp. 1136-1143, (2011)

[10]

Chen X.B., Birbilis N., Abbott T.B., Effect of [Ca2+] and [] levels on the formation of calcium phosphate conversion coatings on die-cast magnesium alloy AZ91D, Corros Sci, 55, pp. 226-232, (2012)

← 1 2 →