Thermal damage analysis of vacuum brazing diamond with Ni-Cr alloy

被引：0
|
作者：
Lu, Jinbin [1 ,2 ]
Tang, Feng [1 ]
Meng, Pu [1 ]
Wang, Zhixin [1 ]
机构：
[1] College of Materials and Chemical Engineering, Zhongyuan University of Technology, Zhengzhou 450007, China
[2] College of Mechanical Engineering, Nanjing University of Aeronautics and Astronautics, Nanjing 210016, China
来源：
Hanjie Xuebao/Transactions of the China Welding Institution | 2010年 / 31卷 / 08期
关键词：
Chromium alloys - Diamonds - Carbides - Brazing - Chemical bonds - Graphitization - Binary alloys - Graphite - Vacuum applications;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Brazing diamond tools has the characteristics of high protrude and strong bonding, which will be significantly degraded in brazing with the excessively high temperature, and so the thermal damage for the diamond was analyzed. The diamond was brazed in vacuum by using Ni-Cr alloy, then the surface of sample was observed by SEM and EDS, and the heat stress and graphitization on the surface were detected with Laser Raman spectroscopy. The results show that more carbide, such as Cr3C2, Cr7C3, exists on the diamond surface, and a little graphitization and chemical soakage take place on the surface. The tensile stress in the top of diamond is 110 MPa, and the compressive stress in the bottom of diamond is 520 MPa.
引用
收藏
页码：25 / 28
相关论文
共 50 条
  • [41] THERMAL DEGRADATION OF NI-CR EUTECTIC
    FUJII, CT
    MEUSSNER, RA
    REPORT OF NRL PROGRESS, 1970, (DEC): : 17 - &
  • [42] Laser brazing of diamond grits with a Ni-based brazing alloy
    Yang, Zhibo
    Xu, Jiuhua
    Fu, Yucan
    Xu, Hongjun
    ADVANCES IN GRINDING AND ABRASIVE TECHNOLOGY XIV, 2008, 359-360 : 43 - 47
  • [43] Interfacial analysis of vacuum brazing diamond/WC mixed abrasives with Ni-Cr-B-Si active filler
    Xiao, Haozhong
    Xiao, Bing
    Liu, Sixing
    Wu, Hengheng
    VACUUM, 2019, 164 : 158 - 164
  • [44] Electrodeposition of Ni-Cr alloy on aluminum substrate
    杨余芳
    龚竹青
    邓丽元
    罗北平
    马玉天
    阳征会
    Journal of Central South University of Technology(English Edition), 2006, (03) : 219 - 224
  • [45] Electrodeposition of Ni-Cr alloy on aluminum substrate
    Yang, Yu-fang
    Gong, Zhu-qing
    Deng, Li-yuan
    Luo, Bei-ping
    Ma, Yu-tian
    Yang, Zhen-hui
    JOURNAL OF CENTRAL SOUTH UNIVERSITY OF TECHNOLOGY, 2006, 13 (03): : 219 - 224
  • [46] CONDITION OF A CHROMIUM ATOM IN NI-CR ALLOY
    KALINOVICH, DF
    KOVENSKII, II
    SMOLIN, MD
    IZVESTIYA VYSSHIKH UCHEBNYKH ZAVEDENII FIZIKA, 1974, (07): : 142 - 144
  • [47] Density of Ni-Cr Alloy in the Mushy State
    Feng XIAO1) Joining and Welding Research Institute
    JournalofMaterialsScience&Technology, 2003, (02) : 107 - 110
  • [48] Electrodeposition and characterization of Ni-Cr alloy coating
    Tharamani, CN
    Hoor, FS
    Begum, NS
    Mayanna, SM
    JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 2006, 153 (03) : C164 - C169
  • [49] Effect of thermal and thermomechanical ageing on the microstructure and mechanical properties of a Ni-Cr alloy
    Chomette, S.
    Gentzbittel, J. M.
    Calapez, J.
    Viguier, B.
    15TH INTERNATIONAL CONFERENCE ON THE STRENGTH OF MATERIALS (ICSMA-15), 2010, 240
  • [50] Density of Ni-Cr alloy in the mushy state
    Xiao, F
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2003, 19 (02) : 107 - 110
12345