Thermal damage analysis of vacuum brazing diamond with Ni-Cr alloy

被引：0
|
作者：
Lu, Jinbin [1 ,2 ]
Tang, Feng [1 ]
Meng, Pu [1 ]
Wang, Zhixin [1 ]
机构：
[1] College of Materials and Chemical Engineering, Zhongyuan University of Technology, Zhengzhou 450007, China
[2] College of Mechanical Engineering, Nanjing University of Aeronautics and Astronautics, Nanjing 210016, China
来源：
Hanjie Xuebao/Transactions of the China Welding Institution | 2010年 / 31卷 / 08期
关键词：
Chromium alloys - Diamonds - Carbides - Brazing - Chemical bonds - Graphitization - Binary alloys - Graphite - Vacuum applications;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Brazing diamond tools has the characteristics of high protrude and strong bonding, which will be significantly degraded in brazing with the excessively high temperature, and so the thermal damage for the diamond was analyzed. The diamond was brazed in vacuum by using Ni-Cr alloy, then the surface of sample was observed by SEM and EDS, and the heat stress and graphitization on the surface were detected with Laser Raman spectroscopy. The results show that more carbide, such as Cr3C2, Cr7C3, exists on the diamond surface, and a little graphitization and chemical soakage take place on the surface. The tensile stress in the top of diamond is 110 MPa, and the compressive stress in the bottom of diamond is 520 MPa.
引用
收藏
页码：25 / 28
相关论文
共 50 条
  • [11] Laser welding and brazing of a Ni-Cr alloy.
    Souza, PCRD
    Dinato, JC
    Bottino, MA
    Nishioka, RS
    Guastaldi, AC
    JOURNAL OF DENTAL RESEARCH, 2001, 80 (04) : 1014 - 1014
  • [12] Microstructure and properties at bonds of diamond grains and Ni-Cr filler alloy by fiber laser brazing
    Zhang, Mingjun
    Li, Xiong
    Mao, Cong
    Hu, Yongle
    Li, Kangwei
    Zhang, Jian
    Tang, Kun
    Bi, Zhuming
    DIAMOND AND RELATED MATERIALS, 2022, 125
  • [13] EXPERIMENTAL INVESTIGATION ON INDUCTION BRAZING OF DIAMOND WITH NI-CR HARDFACING ALLOY UNDER ARGON ATMOSPHERE
    CHATTOPADHYAY, AK
    CHOLLET, L
    HINTERMANN, HE
    JOURNAL OF MATERIALS SCIENCE, 1991, 26 (18) : 5093 - 5100
  • [14] Form and distribution characterization of reaction products at the brazing interface between Ni-Cr alloy and diamond
    Xiao, B
    Xu, HJ
    Fu, YC
    Xu, JH
    ADVANCES IN GRINDING AND ABRASIVE PROCESSES, 2004, 259-2 : 151 - 153
  • [15] Fabrication and performance of brazing diamond using large size Ni-Cr alloy as a bonding agent
    Chen, Zhili
    Xiao, Bing
    Wang, Bo
    DIAMOND AND RELATED MATERIALS, 2021, 115
  • [16] Study on brazing of Ti-coated diamond with Ni-Cr filler
    Department of Materials and Chemical Engineering, Zhongyuan Institute of Technology, ZhengZhqu, Henna 450007, China
    不详
    Jingangshi yu Moliao Moju Gongcheng, 2006, 6 (19-21):
  • [17] Micro-analysis of interface between Ni-Cr alloy and diamond
    Yao, Z.J.
    Xu, H.J.
    Xiao, B.
    Wu, Z.B.
    Nanjing Hangkong Hangtian Daxue Xuebao/Journal of Nanjing University of Aeronautics and Astronautics, 2001, 33 (04):
  • [18] Impact of ultrasonic vibration on microstructure and mechanical properties of diamond in laser brazing with Ni-Cr filler alloy
    Zhang, Mingjun
    Li, Kangwei
    Huang, Yubin
    Hu, Yongle
    Mao, Cong
    Zhang, Jian
    Tong, Yonggang
    Bi, Zhuming
    CERAMICS INTERNATIONAL, 2022, 48 (03) : 4096 - 4104
  • [19] Effect on microstructure for adding graphite to Ni-Cr alloy when brazing diamond abrasive in controlled atmosphere
    Lu, Jinbin
    Zhang, Wangxi
    Zhang, Lei
    Ding, Tianran
    Meng, Pu
    Zhao, Bin
    Jixie Gongcheng Xuebao/Journal of Mechanical Engineering, 2014, 50 (04): : 80 - 84
  • [20] Nucleation and Growth of Cr7c3 of Brazing Diamond with Ni-Cr Alloy in Protective Atmosphere Furnace
    Lu Jin-bin
    Meng Pu
    Zhao Bin
    Liu Jian-jun
    ADVANCED MATERIALS RESEARCH II, PTS 1 AND 2, 2012, 463-464 : 505 - +
12345