Application of multiple integral forging in preparation of wrought superalloy FGH96 turbine disk

被引：0

作者：

Fu R. ^{[1
]}

Li F. ^{[1
]}

Yin F. ^{[1
]}

Feng D. ^{[1
]}

Hao F. ^{[2
]}

Du G. ^{[2
]}

机构：

[1] Department of High-Temperature Materials, Central Iron and Steel Research Institute, Beijing

[2] Western Superconducting Technologies Co., Ltd., Xi'an

来源：

| 1600年 / Editorial Office of Chinese Journal of Rare Metals卷 / 41期

关键词：

Dynamic recrystallization; Electro-slag remelting directionally solidification; Multiple integral forging; Turbine disk; Wrought FGH96;

D O I：

10.13373/j.cnki.cjrm.XY15082802

中图分类号：

学科分类号：

摘要：

What the aeroengine material researchers focus on has always been the uniformity of microstructure and chemistry element in turbine disks with excellent comprehensive mechanical properties. Multiple integral forging is an important processing technology used for obtaining uniform billets with ultrafine grain microstructure, which could effectively improve the microstructure homogeneity and various properties of materials. Based on the electro-slag remelting directionally solidification & wrought FGH96 alloy with low segregation levels and high purity, the deformation mechanism during multiple integral forging for the disk alloy was studied. The results showed that the size of dynamic recrystallized grain increased with the increase of deformation temperature, and the critical cumulative strain required for complete dynamic recrystallization decreased within the sub-solvus temperature range. The desired microstructure with appropriate grain size and second phases was obtained by the control of deformation temperature, rate and cumulative strain during the process of multiple integral forging. Compared to uniaxial forging, multiple integral forging could fully eliminate the forging streamlines, coarse deformed grains and shear zones, which greatly improved the homogeneity of microstructure. Finally, the microstructure during deformation was observed and analyzed to expound the recrystallization mechanism by means of transmission electron microscopy. © Editorial Office of Chinese Journal of Rare Metals. All right reserved.

引用

页码：113 / 119

页数：6

共 23 条

[1]

Reed R.C., The Superalloys Fundamentals and Applications, (2006)

[2]

Furrer D., Fecht H., Ni-based superalloys for turbine discs, Journal of Metals, 51, 1, (1999)

[3]

Ye J., Superalloy of USA, (1978)

[4]

Fu R., Chen X.C., Ren H., Feng D., Structure and hot behavior of ESR-CDS Rene88DT, Journal of Aeronautical Materials, 31, 3, (2011)

[5]

Aude L., Jonathan C., Patrick V., Impact of the solution cooling rate and of thermal aging on the creep properties of the new cast & wrought Rene 65 Ni-based superalloy, 8th International Symposium on Superalloys 718 and Derivatives, (2014)

[6]

Fu R., Research on Process and Technology of ESR-CDS, (2008)

[7]

Guo Q., Yan H.G., Chen Z.H., Zhang H., Research progress in multiple forging process, Material Review, 21, 2, (2007)

[8]

Valiev R.Z., Islamgaliev R.K., Alexandrov I.V., Bulk nanostructured materials from severe plastic deformation, Progress in Materials Science, 45, (2000)

[9]

Taku S., Andrey B., Rustam K., Dynamic and post-dynamic recrystallization under hot, cold and severe plastic deformation conditions, Progress in Materials Science, 60, (2014)

[10]

Imayev R.M., Imayev V.M., Salishchiv G.A., Formation of submicrocrystalline structure in TiAl intermetallic compound, Journal of Material Science, 27, 16, (1991)