Process optimization and microstructural development during superplastic-like forming of AA5083

被引：0
|
作者：
机构：
[1] Liu, Jun
[2] Tan, Ming-Jen
[3] Lim, Chao-Voon S.
[4] Chua, Beng-Wah
来源：
Tan, M.-J. (mmjtan@ntu.edu.sg) | 1600年 / Springer London卷 / 69期
关键词：
An advanced sheet forming process was utilized by combining hot drawing and blow forming to establish a fast forming technology. As a continuation of the development in superplastic-like forming; this study dealt with the process optimization and evaluation of post-forming properties. Aluminum alloy 5083 (AA5083) parts with near-net shape were successfully fabricated at 400 °C. Thickness uniformity has been improved by optimizing the mechanical preforming (hot drawing) and adopting a strain-rate-control gas forming (blow forming). Fairly uniform microstructure can be achieved with this forming process. To investigate the microstructural information; the annealed and hot deformed samples were characterized using electron backscatter diffraction technique. Fine grains with high-angle grain boundaries occurred near the elongated grains during hot drawing stage as a result of dynamic recrystallization. Subgrain structure was also examined by characterizing the distribution of grain boundary misorientation angles. Grain growth and subgrain boundary migration were two main microstructural features observed during the gas forming stage. © Springer-Verlag London 2013;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Journal article (JA)
引用
收藏
页码：9 / 12
相关论文
共 50 条
  • [41] Formability and cavitation behavior of superplastic AA5083 aluminum alloy under biaxial tension
    罗应兵
    李大永
    彭颖红
    TransactionsofNonferrousMetalsSocietyofChina, 2006, (S3) : 1630 - 1633
  • [42] Effects of the temperature of warm rolling on the superplastic behaviour of AA5083 aluminium base alloy
    Pimenoff, J
    Yagodzinskyy, Y
    Romu, J
    Hänninen, H
    SUPERPLASTICITY IN ADVANCED MATERIALS, ICSAM-2000, 2001, 357-3 : 277 - 282
  • [43] Formability Characteristics of AA5083 Sheets Under Hot Forming Conditions
    Bruschi, Stefania
    Ghiotti, Andrea
    Michieletto, Francesco
    SHEET METAL 2013, 2013, 549 : 356 - 363
  • [44] Forming limit diagrams for AA5083 under SPF and QPF conditions
    Kulas, Mary-Anne
    Krajewski, Paul E.
    Bradley, John R.
    Taleff, Eric M.
    SUPERPLASTICITY IN ADVANCED MATERIALS, 2007, 551-552 : 129 - +
  • [45] Microstructural characterization of dissimilar friction stir welds between AA2219 and AA5083
    J. J. S. Dilip
    M. Koilraj
    V. Sundareswaran
    G. D. Janaki Ram
    S. R. Koteswara Rao
    Transactions of the Indian Institute of Metals, 2010, 63 : 757 - 764
  • [46] Microstructure evolution of Ti-6Al-4V during superplastic-like Forming
    20150900571011
    (1) School of Mechanical and Aerospace Engineering, Nanyang Technological University, 639798, Singapore; (2) Singapore Institute of Manufacturing Technology, 71 Nanyang Dr, 638075, Singapore, 1600, (Elsevier Ltd):
  • [47] Microstructural characterization of dissimilar friction stir welds between AA2219 and AA5083
    Dilip, J. J. S.
    Koilraj, M.
    Sundareswaran, V.
    Ram, G. D. Janaki
    Rao, S. R. Koteswara
    TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 2010, 63 (04) : 757 - 764
  • [48] Optimal FSW process parameters for aluminum alloys AA5083
    Chien, Chi-Hui
    Lin, Wei-Bang
    Chen, Thaiping
    JOURNAL OF THE CHINESE INSTITUTE OF ENGINEERS, 2011, 34 (01) : 99 - 105
  • [49] Microstructure evolution of Ti-6Al-4V during superplastic-like forming
    Guo, Mei-Ling
    Liu, Jun
    Tan, Ming-Jen
    Chua, Beng-Wah
    11TH INTERNATIONAL CONFERENCE ON TECHNOLOGY OF PLASTICITY, ICTP 2014, 2014, 81 : 1090 - 1095
  • [50] Synthesis, Microstructural Investigation, and Mechanical Behavior of AA5083/Boron Nitride Nanocomposite
    Ammar, Hany R.
    Sivasankaran, Subbarayan
    ADVANCED ENGINEERING MATERIALS, 2025, 27 (06)
12345