Effect of Solution Treatment Temperature on Microstructure and Mechanical Properties of GH3625 Alloy Hot Extruded Tube

被引：0

作者：

Ding Y. ^{[1
]}

Ma Y. ^{[1
]}

Dou Z. ^{[1
]}

Liu J. ^{[1
]}

Gao Y. ^{[1
]}

Meng B. ^{[1
]}

机构：

[1] State Key Laboratory of Advanced Processing and Recycling of Nonferrous Metals, Lanzhou University of Technology, Lanzhou

来源：

Cailiao Daobao/Materials Review | 2018年 / 32卷 / 04期

关键词：

GH3625; alloy; Mechanical properties; Microstructure; Solution treatment;

D O I：

10.11896/j.issn.1005-023X.2018.08.020

中图分类号：

学科分类号：

摘要：

The influence of solution temperature on microstructure and mechanical properties of GH3625 alloy hot extruded tube were investigated by SEM, EDS, XRD, etc. The results indicated that 1 120℃ was a turning point in the microstructure and mechanical properties of alloys. When the solution treatment temperature was between 910℃ and 1 120℃, the grain hardness increased and the strength decreased slowly because of the pinning of NbC phase at grain boundary. When the solution temperature exceeded 1 120℃, the NbC phase was dissolved in a large amount, the pinning effect was weakened, the grain size increased rapidly, the hardness and strength of the alloy decreased obviously. With the increasing temperature, the dimples in alloy fractwre became large and deep and the plasticity gradually increased. When the temperature exceeded 1 120℃, there were mainly dimples in tensile fracture. In conclusion, the optimum solution treatment temperature of GH3625 alloy hot extrusion tube is 1 120℃. © 2018, Materials Review Magazine. All right reserved.

引用

页码：1311 / 1317

页数：6

共 26 条

[1]

Zhong Z.W., Peng Z.F., Fractal roughness structures of precision-machined WC-Co- and Inconel 625-coated steel rods, The International Journal of Advanced Manufacturing Technology, 33, 9, (2007)

[2]

Thivillon L., Bertrand P.H., Laget B., Et al., Potential of direct metal deposition technology for manufacturing thick functionally graded coatings and parts for reactors components, Journal of Nuclear Materials, 385, 2, (2009)

[3]

Lu Y., Xu F., Liu Y., Et al., Effect of solution temperature on the microstructure of Inconel 625 alloy fabricated by PAW rapid prototyping, Materials Science & Technology, 21, 2, (2013)

[4]

Zhang Q., Wang J.W., Et al., Effects of solution treatment on microstructure and tensile properties of hot isostatic pressed Inconel 625 alloy, Heat Treatment of Metals, 38, 3, (2013)

[5]

Wei P., Li J.R., Zhong Z.G., Study on the surface recrystallization of a nickel-base single crystal superalloy, Journal of Materials Engineering, 10, (2001)

[6]

Cox D.C., Roebuck B., Rae C.M.F., Et al., Recrystallisation of single crystal superalloy CMSX-4, Materials Science and Technology, 19, 4, (2003)

[7]

Li Y.N., He D., Li S.S., Et al., Surface recrystallization in a Ni<sub>3</sub>Al based single crystal alloy IC6sx, Acta Metallurgica Sinica, 44, 4, (2008)

[8]

Wang Z.G., Zhao J.C., Yan P., Et al., Recrystallization of nickel base single crystal superalloy, Journal of Iron & Steel Research, 21, 2, (2009)

[9]

Li J.R., Sun F.L., Xiong J.C., Et al., Effects of surface recrystallization on the microstructures and creep properties of single crystal superalloy DD6, Materials Science Forum, 638-642, 9, (2010)

[10]

Bian F., Su G., Et al., Effect of solution parameters on grain growth of cold deformed Inconel 718 alloy, Rare Metal Materials and Engineering, 34, 8, (2005)

← 1 2 3 →