Impact of Calcium Sulfate on Hydration Features of Calcium Sulfoaluminate Cement

被引：0
|
作者：
Xu L. [1 ]
Zhou X. [2 ]
Li N. [1 ]
Wang P. [1 ]
机构：
[1] Key Laboratory of Advanced Civil Engineering Materials of Ministry of Education, Tongji University, Shanghai
[2] Yunnan Research Institute of Building Science, Kunming
来源：
| 1600年 / Science Press卷 / 45期
关键词：
Alumina gel; Calcium sulfate; Calcium sulfoaluminate cement; Ettringite; Hydration;
D O I：
10.11908/j.issn.0253-374x.2017.06.015
中图分类号：
学科分类号：
摘要：
The impact of calcium sulfate (anhydrite and desulphurization gypsum) on the hydration of calcium sulfoaluminate (CSA) cement, such as compressive strength, drying shrinkage ratio, hydration heat of early stage and microstructure evolution, was measured. Results reveal that, the early hydration of CSA cement is accelerated by the addition of calcium sulfate, resulting in higher 1-day compressive strength and lower drying shrinkage once the dosage is less than 20% (mass ratio). However, with the increasing amount of calcium sulfate, 3-day and 28-day strength is prominently decreased, and even the retraction of strength happens when doping with excessive calcium sulfate. Compressive strength has no direct correlations with ettringite amount, while it has positive correlation with the alumina gel amount. Additionally, to achieve CSA cement with better properties, it is very promising to replace anhydrite with desulphurization gypsum. © 2017, Editorial Department of Journal of Tongji University. All right reserved.
引用
收藏
页码：885 / 890
页数：5
相关论文
共 22 条
  • [1] Su M., Wang Y., Zhang L., Calcium Sulfoaluminate Cement, (1999)
  • [2] Song M.M., Purnell P., Richardson I., Microstructure of interface between fibre and matrix in 10-year aged GRC modified by calcium sulfoaluminate cement, Cement and Concrete Research, 76, (2015)
  • [3] Chaunsali P., Mondal P., Influence of calcium sulfoaluminate (CSA) cement content on expansion and hydration behavior of various ordinary portland cement: CSA blends, Journal of American Ceramic Society, 98, 8, (2015)
  • [4] Brien J.V., Development of cementitious materials for adhesion type applications comprising calcium sulfoaluminate (CSA) cement and latex polymer, (2014)
  • [5] Telesca A., Marroccoli M., Pace M.L., Et al., A hydration study of various calcium sulfoaluminate cements, Cement and Concrete Composites, 53, (2014)
  • [6] Allevi S., Marchi M., Scotti F., Et al., Hydration of calcium sulphoaluminate clinker with additions of different calcium sulphate sources, Materials and Structure, 49, (2016)
  • [7] Han F., Chen H., Li X., Et al., Improvement of mechanical properties of concrete canvas by anhydrite-modified calcium sulfoaluminate cement, Journal of Composite Materials, 50, 14, (2016)
  • [8] Garcia-Mate M., Angeles G., Leon-Reina L., Et al., Effect of calcium sulfate source on the hydration of calcium sulfoaluminate eco-cement, Cement and Concrete Composites, 55, (2015)
  • [9] Trauchessec R., Mechling J.M., Lecomte A., Et al., Impact of anhydrite proportion in a calcium sulfoaluminate cement and Portland cement blend, Advances in Cement Research, 26, 6, (2014)
  • [10] Hargis C.W., Kirchheim A.P., Monteiro P.J.M., Et al., Early age hydration of calcium sulfoaluminate (synthetic ye'elimite) in the presence of gypsum and varying amounts of calcium hydroxide, Cement and Concrete Research, 48, (2013)
123