Experiment Research on Fatigue Performance of Pre-Corroded High-Strength Bridge Wires

被引：0
作者：
Wu C. [1 ]
Jiang C. [1 ]
Jiang X. [1 ]
机构：
[1] College of Civil Engineering, Tongji University, Shanghai
来源：
Tongji Daxue Xuebao/Journal of Tongji University | 2018年 / 46卷 / 12期
关键词：
Corrosion; Fatigue; High-strength bridge wires;
D O I：
10.11908/j.issn.0253-374x.2018.12.002
中图分类号：
学科分类号：
摘要：
In order to investigate the fatigue properties of pre-corroded high-strength bridge wires, a total of 30 steel wire specimens on six corrosion levels were prepared by using the acetic acid salt spray test. Fatigue tests were conducted with the specimens. The effects of corrosion level and stress amplitude were analyzed and the law of fatigue strength degradation was studied. The test results show that the fatigue life of bridge wires decreases significantly under corrosion. Bilinear S-N curves of pre-corroded bridge wires were established and the logarithm of fatigue life decreased linearly with the weight loss at the same stress. Finally, the fatigue surface equations of pre-corroded high-strength bridge wires were established based on the test results and the recommended fatigue strength at different assure rates were proposed. © 2018, Editorial Department of Journal of Tongji University. All right reserved.
引用
收藏
页码：1622 / 1627and1695
相关论文
共 16 条
  • [1] Wang L., Yi W., Cases analysis on cable corrosion of cable stayed bridges, Central South Highway Engineering, 32, 1, (2007)
  • [2] Xu J., Damage evolution mechanism and remained service lives evaluation of stayed cables, (2006)
  • [3] Li S., Xu Y., Li H., Et al., Uniform and pitting corrosion modeling for high-strength bridge wires, Journal of Bridge Engineering, 19, 7, (2014)
  • [4] Betti R., West A.C., Vermaas G., Et al., Corrosion and embrittlement in high-strength wires of suspension bridge cables, Journal of Bridge Engineering, 10, 2, (2005)
  • [5] Nakamura S.-I., Suzumura K., Tarui T., Mechanical properties and remaining strength of corroded bridge wires, Structural Engineering International, 14, 1, (2004)
  • [6] Li S., Xu Y., Zhu S., Et al., Probabilistic deterioration model of high-strength steel wires and its application to bridge cables, Structure & Infrastructure Engineering, 11, 9, (2014)
  • [7] Nakamura S.-I., Suzumura K., Experimental study on fatigue strength of corroded bridge wires, Journal of Bridge Engineering, 18, 3, (2013)
  • [8] Li H., Lan C.M., Ju Y., Et al., Experimental and numerical study of the fatigue properties of corroded parallel wire cables, Journal of Bridge Engineering, 17, 2, (2011)
  • [9] Sun C., Assessment of safety capability and fatigue life of corroded cable for cable-supported bridge, (2013)
  • [10] Zheng X., Xie X., Li X., Et al., Fatigue fracture surface analysis and fatigue life estimation of corroded steel wires, China Journal of Highway and Transport, 30, 4, (2017)
12