Corrosion behavior of A6061 aluminum alloy in cation containing aqueous medium

被引：0
|
作者：
MdSaiful Islam [1 ,2 ]
Masatoshi Sakairi [3 ]
机构：
[1] Department of Applied Chemistry & Chemical Engineering, University of Rajshahi
[2] Graduate School of Engineering, Hokkaido University
[3] Faculty of Engineering, Hokkaido
来源：
Corrosion Communications | 2022年 / 5卷 / 01期
关键词：
D O I：
暂无
中图分类号：
TG172 [各种类型的金属腐蚀];
学科分类号：
摘要：
Corrosion behavior of A6061 aluminum alloy in cation containing simulated aqueous medium was investigated by surface analysis techniques and electrochemical tests.The mass of specimens was increased after the immersion tests,and a smaller mass change was observed in the Zn2+containing solution.Electron microscopic images showed the deposited products on the specimen that were Al-hydroxide confirmed by X-ray photoelectron spectroscopy.Zn-layer was formed on the specimen immersed in Zn2+containing solution,and corrosion inhibition of Al resulted in a smaller number of Al products deposited on the alloy surface.Electrochemical results showed higher impedance in the Zn2+containing solution due to the formation of the Zn related layer on the surface with oxide film.
引用
收藏
页码：39 / 48
页数：10
相关论文
共 50 条
  • [1] Corrosion behavior of A6061 aluminum alloy in cation containing aqueous medium
    Islam, Md. Saiful
    Sakairi, Masatoshi
    CORROSION COMMUNICATIONS, 2022, 5 : 39 - 48
  • [2] Edge Joining of A6061 Aluminum Alloy Sheets by Electrodeposition of Copper
    Hakamada, Masataka
    Hirose, Soya
    Yamamoto, Yuki
    Huang, Xinsheng
    Nakatsugawa, Isao
    Chino, Yasumasa
    Nakano, Hiromi
    Mabuchi, Mamoru
    Materials Transactions, 2023, 64 (10): : 2328 - 2332
  • [3] ORIENTATION DISTRIBUTION IN FRICTION STIR PROCESSED A6061 ALUMINUM ALLOY
    Shibayanagi, Toshiya
    Matsumoto, Takamasa
    CHARACTERIZATION AND CONTROL OF INTERFACES FOR HIGH QUALITY ADVANCED MATERIALS II, 2007, 198 : 103 - +
  • [4] Edge Joining of A6061 Aluminum Alloy Sheets by Electrodeposition of Copper
    Hakamada, Masataka
    Hirose, Soya
    Yamamoto, Yuki
    Huang, Xinsheng
    Nakatsugawa, Isao
    Chino, Yasumasa
    Nakano, Hiromi
    Mabuchi, Mamoru
    MATERIALS TRANSACTIONS, 2023, 64 (09) : 2328 - 2332
  • [5] Growth behavior of pores and hydrogen desorption behavior in pure aluminum and A6061 aluminum alloys
    Yaegashi S.
    Shimizu K.
    Kamada Y.
    Toda H.
    Fujihara H.
    Uesugi M.
    Takeuchi A.
    Keikinzoku/Journal of Japan Institute of Light Metals, 2023, 73 (05): : 212 - 217
  • [6] Effect of anodizing pretreatment on laser joining CFRP to aluminum alloy A6061
    Zhang, Zhou
    Shan, Ji-Guo
    Tan, Xiang-Hu
    Zhang, Jing
    INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES, 2016, 70 : 142 - 151
  • [7] Effect of Ultrasonic Rolling on Intergranular Corrosion Behavior of 6061 Aluminum Alloy
    Hu Z.-Y.
    Shi W.
    Xiang S.
    Surface Technology, 2023, 52 (10): : 194 - 205
  • [8] MIXED MODE FRACTURE BEHAVIOR OF AN ALUMINUM ALLOY A6061 INVESTIGATED BY USING COMPACT TENSION SHEAR SPECIMENS
    Husaini
    Zuhaimi
    INTERNATIONAL JOURNAL OF TECHNOLOGY, 2016, 7 (03) : 456 - 462
  • [9] Unveiling Thermal and Athermal Effects in Strain Hardening Removal of A6061 Aluminum Alloy
    Yu, Xiaoming
    Gu, Shaojie
    Wang, Guodong
    Kimura, Yasuhiro
    Ju, Yang
    Toku, Yuhki
    METALS AND MATERIALS INTERNATIONAL, 2025, 31 (03) : 654 - 665
  • [10] Effects of Picture Frame Technique (PFT) on the corrosion behavior of 6061 aluminum alloy
    Milagre, Mariana X.
    Donatus, Uyime
    Mogili, Naga, V
    Machado, Caruline S. C.
    Araujo, Joao Victor S.
    Klumpp, Rafael E.
    Fernandes, Stela M. C.
    Souza, Jose A. B. de
    Costa, Isolda
    JOURNAL OF NUCLEAR MATERIALS, 2020, 539
12345