Hydrogenation behavior of Cr-coated laser beam welds of E110 zirconium alloy

被引：0

作者：

Kashkarov E.B. ^{[1
]}

Kudiiarov V.N. ^{[1
]}

Kurdyumov N. ^{[1
]}

Krinitcyn M.G. ^{[1
,2
]}

Sidelev D.V. ^{[1
]}

机构：

[1] National Research Tomsk Polytechnic University, Tomsk

[2] Institute of Strength Physics and Materials Science SB RAS, Tomsk

来源：

Journal of Nuclear Materials | 2022年 / 570卷

基金：

俄罗斯科学基金会;

关键词：

Accident tolerant fuel; Hydrogenation; Laser beam welding; Magnetron sputtering; Protective coatings; Zirconium alloys;

D O I：

10.1016/j.jnucmat.2022.153980

中图分类号：

学科分类号：

摘要：

The influence of chromium coating on hydrogenation behavior of laser beam welds (LBW) of E110 zirconium alloy was studied at 360–900 °C and hydrogen pressure of 2 bar. The deposition of Cr coating can slow down hydrogen absorption rate of the LBW samples as activation energy for hydrogen absorption (70 kJ/mol) is higher compared to uncoated ones (61 kJ/mol). The growth of hydrides depends on the hydrogenation conditions and original microstructure of welded alloy in different zones. Nanoindentation and three-point bending tests show that hydride precipitations can cause hardening of LBW E110 alloy samples and loss of its plasticity. Some additional aspects of applying Cr coatings for protection of LBW Zr alloy in hydrogen atmosphere are presented. © 2022 Elsevier B.V.

引用

共 50 条

[31] Graphene protective coatings for hydrogen resistance improving of E110 zirconium alloy
Kudiiarov, Viktor N.
Anzhigatova, Elena D.
Kurdyumov, Nikita E.
Kashkarov, Egor B.
V. Smovzh, Dmitriy
V. Sorokin, Dmitry
Skirda, Mikhail S.
PHYSICA B-CONDENSED MATTER, 2024, 694
[32] Oxidation behavior of Cr-coated zirconium alloy cladding in high-temperature steam above 1200 °C
Hai-Bin Ma
Jun Yan
Ya-Huan Zhao
Tong Liu
Qi-Sen Ren
Ye-Hong Liao
Jia-Dong Zuo
Gang Liu
Mei-Yi Yao
npj Materials Degradation, 5
[33] Identification of Optimum Laser Beam Welding Process Parameters for E110 Zirconium Alloy Butt Joint Based on Taguchi-CFD Simulations
Satyanarayana G.
Narayana K.L.
Nageswara Rao B.
Lasers in Manufacturing and Materials Processing, 2018, 5 (2) : 182 - 199
[34] Experimental Study of Cr-coated Zirconium Alloy Cladding under Simulated LOCA Conditions
Wang, Zhanwei
Yan, Jun
Peng, Zhenxun
Ren, Qisen
Liao, Yehong
Li, Sigong
Zhao, Yahuan
Hedongli Gongcheng/Nuclear Power Engineering, 2023, 44 (02): : 122 - 128
[35] Corrosion and high-temperature steam oxidation of E110 alloy and its laser welds after ion irradiation
Slobodyan, Mikhail S.
Pavlov, Sergey K.
Remnev, Gennady E.
CORROSION SCIENCE, 2019, 152 : 60 - 74
[36] Evolution of Cr/Cr2O3 interface in Cr-coated zirconium alloy in high temperature steam
Wang, Yao
Chen, Bo
Wang, Xian-Zong
Chen, Mingju
Li, Shilei
Bai, Guanghai
Li, Jinshan
Gong, Weijia
CORROSION SCIENCE, 2023, 217
[37] Influence of Chromium Coating on Microstructure Changes in Zirconium Alloy E110 Under High-Temperature Hydrogenation and Kr Ion Irradiation
Kruglyakov, Mark A.
Kudiiarov, Viktor N.
Laptev, Roman S.
Vrublevskii, Dmitrii B.
Svyatkin, Leonid A.
Uglov, Vladimir V.
Ivanov, Igor A.
Koloberdin, Mikhail V.
COATINGS, 2025, 15 (02):
[38] Improving fatigue performance of Cr-coated zirconium alloy cladding by ultrasonic shot-peening proces
Wang, Yong-jing
Li, Si -gong
Liu, Yang
Zhang, Zhi-jia
Feng, Rui-xuan
Wang, Qu-ge
Zhang, Qian-cheng
JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2023, 27 : 6047 - 6057
[39] Steam oxidation of Cr-coated zirconium alloy claddings at 1200 °C: Kinetics transition and failure mechanism of Cr coatings
Deng, Jianxi
Geng, Donghui
Sun, Qiaoyan
Song, Zhongxiao
Sun, Jun
JOURNAL OF NUCLEAR MATERIALS, 2023, 586
[40] The oxidation-dissolution behavior of Cr-coated Zr alloy in high temperature water
Huang, Tao
Zhou, Yuhao
Chen, Kai
Wei, Tianguo
Gao, Shixin
Pang, Hua
Yue, Huifang
Zhang, Kun
Shen, Zhao
Zhang, Lefu
JOURNAL OF NUCLEAR MATERIALS, 2025, 604

← 1 2 3 4 5 →