Failure Mode of Thermal Barrier Coatings Based on Acoustic Emission Under Three-Point Bending via Machine Learning Based on in-situ Acoustic Emission Signals

被引：0

作者：

Cao Z. ^{[1
,2
]}

Yuan J. ^{[1
]}

Su H. ^{[2
]}

Wan J. ^{[2
]}

Su J. ^{[2
]}

Wu Q. ^{[2
]}

Wang L. ^{[2
]}

机构：

[1] School of Materials Science and Engineering, Shanghai University of Engineering Science, Shanghai

[2] Integrated Computational Materials Research Center, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai

来源：

Kuei Suan Jen Hsueh Pao/Journal of the Chinese Ceramic Society | 2023年 / 51卷 / 02期

关键词：

acoustic emission; back propagation neural network; failure mode; thermal barrier coating; three-point bending;

D O I：

10.14062/j.issn.0454-5648.20220928

中图分类号：

学科分类号：

摘要：

It is ready to cause the interface delamination, macroscopic fracture and spalling failure of thermal barrier coatings (TBCs) due to their complexity of architecture and harsh service environment. In this paper, the failure process of TBCs under three-point bending (3PB) load was monitored in real time via acoustic emission (AE) technology, and the damage failure modes of TBCs were identified based on micro-morphology analysis of AE parameters and K-means cluster. The waveform characteristics of four failure modes were analyzed by fast Fourier transform and wavelet packet transform. The macroscopic fracture or spalling failure signals have no obvious frequency band, while the corresponding frequency components of substrate deformation, surface vertical crack, sliding interface crack and opening interface crack are 62.5-125.0 kHz, 187.5-250.0 kHz, 250.0-312.5 kHz and 375.0-437.5 kHz, respectively. The method of deep machine learning was used to process the in-situ acoustic emission signals. The wavelet energy coefficient was extracted as a characteristic vector of the Back propagation neural network, and the advantages and disadvantages of the model were evaluated by convergence curve, confusion matrix, Receiver operating characteristic curve and F1 value, thus realizing the discrimination of failure modes of TBCs under 3PB test and providing a reference value for failure prediction and life assessment of thermal barrier coatings. © 2023 Chinese Ceramic Society. All rights reserved.

引用

页码：373 / 388

页数：15

共 25 条

[1]

PADTURE N P, GELL M, JORDAN E H., Materials science-thermal barrier coatings for gas-turbine engine applications, Science, 296, 5566, pp. 280-284, (2002)

[2]

XU Binshi, LI Changjiu, LIU Shican, Et al., China Surface Eng, 1, pp. 3-9, (1998)

[3]

YANG Li, ZHOU Yichun, ZHU Wang, Mater Chin, 39, 11, pp. 878-896, (2020)

[4]

HU Zhongchao, WANG Liang, ZHUANG Mingxiang, Et al., Mater Chin (in Chinese), 39, 10, pp. 740-753, (2020)

[5]

CHEN W, LIU M, ZHANG J., Microstructure evolution and impedance spectroscopy analysis of 7YSZ thermal barrier coating during high-temperature oxidation process, Chin Surface Eng, 29, 3, pp. 48-56, (2016)

[6]

ROSSMANN L, NORTHAM M, SARLEY B, Et al., Investigation of TGO stress in thermally cycled plasma-spray physical vapor deposition and electron-beam physical vapor deposition thermal barrier coatings via photoluminescence spectroscopy, Surf Coat Tech, 378, (2019)

[7]

HALLOUA H, ELHASSNAOUI A, SAIFI A, Et al., Neural networks and genetic algorithms for the evaluation of coatings thicknesses in thermal barriers by infrared thermography data, proceedings of the 2nd International Conference on Structural Integrity (ICSI), (2017)

[8]

PARK J H, KIM J S, LEE K H., Acoustic emission characteristics for diagnosis of TBC damaged by high-temperature thermal fatigue, J Mater Process Technol, 187, pp. 537-541, (2007)

[9]

YANG L, KANG H S, ZHOU Y C, Et al., Frequency as a key parameter in discriminating the failure types of thermal barrier coatings: Cluster analysis of acoustic emission signals, Surf Coat Tech, 264, pp. 97-104, (2015)

[10]

YANG L, YANG T T, ZHOU Y C, Et al., Acoustic emission monitoring and damage mode discrimination of APS thermal barrier coatings under high temperature CMAS corrosion, Surf Coat Tech, 304, pp. 272-282, (2016)

← 1 2 3 →