Influence of Admixture on Property of Radioactive Fluoride Liquid Waste Solidified Form by MKPC

被引：0

作者：

Qian Z. ^{[1
]}

Liu X. ^{[1
]}

Qiao Y. ^{[1
]}

Wang S. ^{[1
]}

Qin Q. ^{[1
]}

机构：

[1] Shanghai Institute of Applied Physics, Chinese Academy of Sciences, Shanghai

来源：

Yuanzineng Kexue Jishu/Atomic Energy Science and Technology | 2019年 / 53卷 / 05期

关键词：

Admixture; Magnesium potassium phosphate cementitious material; Radioactive fluoride liquid waste; Solidification;

D O I：

10.7538/yzk.2018.youxian.0442

中图分类号：

学科分类号：

摘要：

In this paper, magnesium potassium phosphate cementitious (MKPC) material was preparaed by adding KH2PO4, dead-burned MgO and borax in a certain proportion to solidify simulated radioactive fluoride liquid waste. The influence of admixtures, such as quartz sand, zeolite, silica fume and fly ash, in the solidified forms was studied. The results show that admixtures don't change the setting time of the solidified form, but influence its porosity. The porosity increases obviously after adding silica fume and decreases after adding fly ash. After cured 28 d, the compressive strength of the solidified forms is greater than 55 MPa. The loss rate of the compressive strength is proportional to porosity. The solidified forms prepared in this paper have good leaching resistance property. After 42 d leaching test, the leaching rate of simulated nuclides Sr2+, Cs+, Co2+ and the 42 d cumulative leaching rate of simulated nuclide Cs+ are lower than the limit value of GB 14569.1-2011. Average leaching concentration of F- is lower than the limit value of GB 5085.3-2007. © 2019, Editorial Board of Atomic Energy Science and Technology. All right reserved.

引用

页码：805 / 810

页数：5

共 12 条

[1]

Williams D.F., Peretz F.J., Characterization of the molten salt reactor experiment fuel and flush salts, American Nuclear Society Meeting, (1996)

[2]

Covill A., Hyatt N.C., Hill J., Et al., Development of magnesium phosphate cements for encapsulation of radioactive waste, Advances in Applied Ceramics, 110, 3, pp. 151-156, (2011)

[3]

Singh D., Wagh A., Cunnane A.C., Chemically bonded phosphate ceramics for low-level mixed-waste stabilization, Journal of Environmental Science and Health A, 32, 2, pp. 527-541, (1997)

[4]

Ding Z., Dong B., Xing F., Et al., Cementing mechanism of potassium phosphate based magnesium phosphate cement, Ceramics International, 38, 8, pp. 6281-6288, (2012)

[5]

Lai Z., Qian J., Liang P., Et al., Study of solidification performance of phosphate cement to <sup>90</sup>Sr, Acta Scientiae Circumstantiae, 31, 12, pp. 2792-2797, (2011)

[6]

Covill A., Hyatt N.C., Hill J., Et al., Development of magnesium phosphate cements for encapsulation of radioactive waste, Advances in Applied Ceramics, 110, 3, pp. 151-156, (2011)

[7]

Dai F., Wang H., Zhang S., Et al., Influence of solidifying simulated radionuclide Sr on hydration characteristics of magnesium phosphate cement, Journal of the Chinese Ceramic Society, 45, 5, pp. 651-656, (2017)

[8]

Langton C.A., Stefanko D.B., Serrato M., Et al., Use of cementitious materials for SRS reactor facility in-situ decommissioning, WM2011 Conference, (2011)

[9]

Cantrell K.J., Um W., Williams B.D., Et al., Chemical stabilization of Hanford tank residual waste, Journal of Nuclear Materials, 446, pp. 246-256, (2014)

[10]

Zhen S., Dong X., Nkrumah P.N., Et al., Effects of fly ash on the solidification/stabilization of heavy metals with magnesium potassium phosphate cement, International Journal of Earth Sciences and Engineering, 7, 4, pp. 1274-1279, (2014)

← 1 2 →