Electrocinder deposition with 110G13L steel chips at a current-supplying crystallizer

被引：0

作者：

Kuskov Y.M. ^{[1
]}

Bogaychuk I.L. ^{[1
]}

Shevchenko N.P. ^{[2
]}

Fesenko M.A. ^{[3
]}

机构：

[1] Paton Electric Welding Institute, NAS Ukraine, Kyiv

[2] Instrument-Servis ChPP, Dnepr

[3] Ukraine Scientific-Technical University Igorya Sikorskogo, Kyiv

来源：

Welding International | 2021年 / 35卷 / 1-3期

关键词：

current-carrying mould; Electroslag surfacing; macro and microstructures; parent steel from steel St3; steel shavings 110G13l;

D O I：

10.1080/09507116.2021.1945318

中图分类号：

学科分类号：

摘要：

Electroslag surfacing was performed in a current-carrying mould of ∅180 mm with 110G13L steel chips on St3 steel billets. It was established that the structure of the deposited metal corresponds to the structure of cast steel, in which austenite is the main phase. It has been shown that the most dangerous zone for the appearance of cracks is the fusion zone of the base and building metal with the formation of a martensitic-bainitic structure and carbides in it. To exclude this zone or reduce its width, surfacing must be performed with the optimal combination of electrical energy introduced into the slag bath and the mass flow rate of the chips. The proposed technology is recommended for the manufacture of bimetallic products operating in conditions of wear and increased shock loads. At the same time, to increase their mechanical properties, it is necessary to provide for heat treatment. © 2021 Informa UK Limited, trading as Taylor & Francis Group.

引用

页码：85 / 90

页数：5

共 9 条

[1] Budanov E.V., Production of castings from 110G13L steel by vacuum-film moulding technology, Liteinoe Proizvodstvo, 9, pp. 28-31, (2014)
[2] Kamyshina K.P., Petrov Y.N., Khomyakov N.F., Wear-resistant steels for various service conditions, Liteinoe proizvodstvo, 7, pp. 2-3, (2000)
[3] Medovar B.I., Ksendzyk G.V., Electroslag remelting of austenitic steel G13, Avtomaticheskaya svarka, 9, pp. 18-21, (1962)
[4] Valits K.A., Shvartser A.Y., Koritskii G.G., Restoration of components made of 110G13L high-manganese steel by electroslag surfacing, Avtomaticheskaya svarka, 5, pp. 64-65, (1989)
[5] Valits K.A., Shvartser A.Y., Stoiko V.P., Flux for electroslag surfacing of high-manganese steel, Problemy spetsial’noi elektrometallurgii, 4, pp. 26-28, (1985)
[6] Valits K.A., Shvartser A.Y., Electroslag surfacing of excavator bucket teeth with steel 110G13L, Avtomaticheskaya svarka, 3, pp. 26-29, (1987)
[7] Kuskov Y.M., Resource-sparing technology for restoring and manufacturing components by electroslag surfacing, Tekhnol mashinostroeniya, 6, pp. 40-42, (2006)
[8] Kuskov Y.M., Discrete filler materials for surfacing in a current supplying mould, Avtomaticheskaya svarka, 6-7, pp. 101-106, (2014)
[9] Yushchenko K.A., Fadeeva G.V., Shevchuk T.V., Causes of microcracking in the HAZ in the welding of 110G13L steel, Avtomaticheskaya svarka, 5-6, pp. 28-31, (1994)

← 1 →