Form-stable phase change materials from mesoporous balsa after selective removal of lignin

被引：0
|
作者：
Meng, Yang [1 ,2 ]
Majoinen, Johanna [1 ]
Zhao, Bin [1 ]
Rojas, Orlando J. [1 ,3 ,4 ,5 ]
机构：
[1] Department of Bioproducts and Biosystems, School of Chemical Engineering, Aalto University, P.O. Box 16300, Espoo,Aalto,FIN-00076, Finland
[2] College of Materials Science and Technology, Beijing Forestry University, No.35, Qinghua East Road, Haidian District, Beijing,100083, China
[3] Department of Chemical & Biological Engineering, The University of British Columbia, 2360 East Mall, Vancouver,BC,V6T 1Z3, Canada
[4] Department of Chemistry, The University of British Columbia, 2036 Main Mall, BC,V6T 1Z1, Canada
[5] Department of Wood Science, The University of British Columbia, 2900-2424 Main Mall, BC,V6T 1Z4, Canada
来源：
Composites Part B: Engineering | 2021年 / 199卷
关键词：
We produce balsa-based structures by selective removal of lignin. The changes that occur in the main components of balsa upon delignification; including tracheids; closed pits and tylosis vessels; allow the development of mesopores and a substantial increase in fluid permeability. Such system is ideally suited as a support of phase change materials; PCM. Vacuum-assisted impregnation with polyethylene glycol (PEG; a PCM); results in a form-stable PCM system (FPCM). The FPCM displays a high encapsulating capacity (83.5%) at temperatures above the melting PEG transition; with a latent heat of 134 J/g and low supercooling (12 °C). The results are rationalized by the affinity between the unidirectional mesoporous structure and the PCM polymer; involving capillary forces and hydrogen bonding. The leakage-proof FPCM outperforms available systems (based on PEG or other PCMs) supported on minerals or other wood species. Compared to the latter group; the results obtained with balsa relate to its morphology and the effect of residual hemicelluloses in hierarchically-aligned cellulose nano- and microfibrils. The FPCMs resist compressive loads and performs stably for at least 200 cycles of heating and cooling. An insignificant loss in latent heat is observed compared to that of pure PEG. The phase transition temperature fluctuation and non-leaking characteristics under load make the balsa-based FPCM a superior alternative for passive heating/cooling; especially for uses at high ambient temperatures. The reversible thermoregulatory capacity; low cost; high efficiency; renewability; and operability of the balsa-supported FPCM; indicate an excellent option for thermal energy storage and conversion devices. © 2020;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
引用
收藏
相关论文
共 50 条
  • [21] Form-stable microencapsulated phase change materials for efficient solar thermal energy storage
    Hu, Heng
    Zhang, Haili
    Hong, Shuliang
    MATERIALS LETTERS, 2023, 352
  • [22] Kaolinite-based form-stable phase change materials for thermal energy storage
    Cheng, Hongfei
    Zhou, Yi
    Xu, Peijie
    Zhang, Meng
    Sun, Luyi
    JOURNAL OF ENERGY STORAGE, 2024, 87
  • [23] Preparation and Characterization of Superporous Hydrogel/Carbon Nano Form-stable Phase Change Materials
    Wang, Ting
    Qiu, Xiao-Lin
    Lu, Li-Xin
    Zhou, Bing-Lin
    Jingxi Huagong/Fine Chemicals, 2019, 36 (11): : 2199 - 2206
  • [24] Erythritol/expanded graphite form-stable phase change materials with excellent thermophysical properties
    Yan, Kening
    Qiu, Lin
    Feng, Yanhui
    JOURNAL OF ENERGY STORAGE, 2023, 68
  • [25] Preparation and Characterization of Form-stable Phase Change Materials with Hydrogel Skeleton as Supporting Material
    Zhang, Yi-hong
    Chen, Yu-yang
    Tu, Long-long
    Zuo, Xue
    Tan, Ye
    Yu, Lin-ping
    Li, Chuan-chang
    Zeng, Ju-lan
    ACTA POLYMERICA SINICA, 2024, 55 (09): : 1229 - 1240
  • [26] Novel hybrid form-stable polyether phase change materials with good fire resistance
    Zhang, Yuang
    Tang, Bingtao
    Wang, Lingjuan
    Lu, Rongwen
    Zhao, Defeng
    Zhang, Shufen
    ENERGY STORAGE MATERIALS, 2017, 6 : 46 - 52
  • [27] Study on phase change materials integration in concrete: Form-stable PCM and direct addition
    Jia, Zhiyou
    Cunha, Sandra
    Aguiar, Jose
    PROCESS SAFETY AND ENVIRONMENTAL PROTECTION, 2024, 189 : 1293 - 1302
  • [28] Preparation and performances of palmitic acid/diatomite form-stable composite phase change materials
    Jia, Wenbing
    Wang, Chaoming
    Wang, Tingjun
    Cai, Zhengyu
    Chen, Ke
    INTERNATIONAL JOURNAL OF ENERGY RESEARCH, 2020, 44 (06) : 4298 - 4308
  • [29] Freeze-cast form-stable phase change materials for thermal energy storage
    Noel, John A.
    White, Mary Anne
    SOLAR ENERGY MATERIALS AND SOLAR CELLS, 2021, 223
  • [30] Lignin-g-polycaprolactone as a form-stable phase change material for thermal energy storage application
    Lee, Johnathan Joo Cheng
    Sugiarto, Sigit
    Ong, Pin Jin
    Soo, Xiang Yun Debbie
    Ni, Xiping
    Luo, Ping
    Hnin, Yu Yu Ko
    See, Josephine Si Yu
    Wei, Fengxia
    Zheng, Rongyan
    Wang, Pei
    Xu, Jianwei
    Loh, Xian Jun
    Kai, Dan
    Zhu, Qiang
    JOURNAL OF ENERGY STORAGE, 2022, 56
12345