Friction stir welding of aluminium and copper alloys

被引：0

作者：

Chularis A.A. ^{[1
]}

Rzaev R.A. ^{[2
]}

Syndetov M.K. ^{[2
]}

机构：

[1] Don State Technical University, Rostov-na-Donu

[2] Astrakhan State University, Astrakhan

来源：

Welding International | 2020年 / 34卷 / 4-6期

关键词：

aluminium alloy; composition; Copper alloy; friction stir welding; mechanical properties; microstructure; phase;

D O I：

10.1080/09507116.2021.1906576

中图分类号：

学科分类号：

摘要：

Sheet blanks from copper (M1) and aluminium alloys (AD1, AD32) with a thickness of 3 mm are joined in butt joints and overlap, butt joints–overlap joints by friction stir welding (FSW). The microstructure, mechanical properties and phase components of the welded joints obtained by the FSW are studied by using various methods of metal physics analysis, including X-ray diffraction, mechanical tensile and bending tests, etc. The test results showed that high quality of the welded joint can be achieved when tool rotation is 900 min–1 and the welding speed is 25 mm/min when the angle of tool inclination angle is 3°. The maximum value of the tensile strength is about 66 MPa. Copper and aluminium alloys are formed due to solid-phase mixing in the superplastic state (SPS), forming a characteristic shear-strip-layered structure with alternating layers in zone of weld seam cores (WSC). A mixed structure with characteristic fragments of Cu and Al is formed on the aluminium side on the side of the WSC. New intermetallic phases were not detected in the WSC centre. © 2021 Informa UK Limited, trading as Taylor & Francis Group.

引用

页码：230 / 241

页数：11

共 32 条

[1]

Larikov L.N., Lozovskaya A.V., Polishchuk V.F., Kinetics of the formation of intermetallic compounds in the copper-aluminium system, pp. 5-49, (1969)

[2]

Rabkin D.M., Ryabov V.R., Lozovskaya A.V., Obtaining and research of properties of intermetallic compounds of the copper-aluminium system, Poroshkovaya Metallurgiya, 8, pp. 101-107, (1970)

[3]

Kornilov I.I., Matveeva N.M., Pryakhina L.I., Et al., The metallochemical properties of the elements of the periodic systems, (1966)

[4]

Larikov L.N., Ryabov V.R., Falchenko V.M., Diffusion Processes in the Solid Phase during Welding, (1975)

[5]

Hansen M., Anderko K., Structure of binary alloys, (1962)

[6]

Drits M.K., Bochvar N.R., Guzei L.S., Binary and multicomponent systems based on copper: handbook, (1979)

[7]

Sinelnikova V.S., Aluminates, (1965)

[8]

Zhang Q., Gong W., Liu W., Microstructure and mechanical properties of dissimilar Al-Cu joints by friction stir welding, Trans Nonferrous Met Soc China, 25, 6, pp. 1779-1786, (2015)

[9]

Feng J., Song-bai X., Ji-yuan L., Et al., Microstructure and properties of Al/Cu joints brazed with Zn-Al filler metals, Trans Nonferrous Met Soc China, 1, pp. 281-287, (2012)

[10]

Weigl M., Albert F., Schmidt M., Enhancing the ductility of laser-welded copper-aluminium joints by using adapted filler materials, Phys Procedia, 12, pp. 335-341, (2011)

← 1 2 3 4 →