The effect of hot dip galvanizing temperature to corrosion rate of steel as the material for chopper machine

被引：4

作者：

Gapsari F. ^{[1
]}

Setyarini P.H. ^{[1
]}

Anam K. ^{[1
]}

Azizah S. ^{[2
]}

Yuliati R. ^{[3
]}

机构：

[1] Mechanical Engineering Department, Brawijaya University, MT Haryono 167, Malang

[2] Faculty of Animal Husbandary, Brawijaya University, Veteran, Malang

[3] Faculty of Cultral Studies, Brawijaya University, Veteran, Malang

来源：

Solid State Phenomena | 2019年 / 291卷

关键词：

Chopper; Corrosion; Hot dip galvanizing; Steel; Zinc;

D O I：

10.4028/www.scientific.net/SSP.291.148

中图分类号：

学科分类号：

摘要：

This study aims to find material steel for animal feed chopper machine which is not easily corroded with method of hot dip galvanizing (HDG). Steel as machinery components or construction often gets broken before the predicted time because of corrosion. The HDG method was begun by pre-treatment process which were polishing, degreasing, rinsing I, pickling, rinsing II, fluxing, and drying. The main process of galvanizing was done by dipping in 98% of zinc solution with temperature variation of 430, 450, 470, and 490°C. The coating thickness measurement was run with Coating thickness NOVOTEST TP-1M. The corrosion was tested with electrochemical method of potentiodynamic polarization with AUTOLAB PGSTAT 128. The highest value of coating thickness was at galvanized temperature of 490°C which was 88.9 ± 3.24%. The value of standard deviation was indicated by how much the coating homogeneity formed. This was in line with the amount of corrosion rate at galvanized temperature of 490°C. The highest corrosion rate values in H2SO4 and NaCl environment were 1.18 and 0.21 mm/year. The highest hardness value of Zn layer is galvanizing temperature of 490°C which rises 41.71% of the base metal. The coating thickness, corrosion and surface hardness test have thee good agreement. © 2019 Trans Tech Publications Ltd, Switzerland.

引用

页码：148 / 154

页数：6

共 23 条

[1]

Gapsari F., Wahyudisumawan S., The Influence of High Content of Silicon in Austenitic Stainless Steel to Corrosion Rate in Sulphuric Acid, Applied Mechanics and Materials, 493, pp. 727-732, (2014)

[2]

Gapsari F., Andokowijaya H., Corrosion Behavior of Brass Acid, Metalurgija, 57, pp. 333-336, (2018)

[3]

Bashi S.M., Mailah N.F., Radzi M.A.M., Cathodic protection system, Proceed of the National Power & Energy Conference, pp. 366-370, (2003)

[4]

Kim I.-D., Nho E.-C., Module-Type Switching Rectifier for Cathodic Protection of Underground and Maritime Metallic Structures, IEEE Transactions on Industrial Electronics, 52, 1, pp. 181-189, (2005)

[5]

Gapsari F., Soenoko R., Suprapto A., Suprapto W., Green Inhibitor For Api 5L X65 Steel In HCl 0.5 M, ARPN Journal of Engineering and Applied Sciences, 11, 15, pp. 9524-9527, (2016)

[6]

Gapsari F., Soenoko R., Suprapto A., Suprapto W., Effect of Organics Corrosion Inhibitors on the Corrosion of 304SS in 3.5% NaCl, International Review of Mechanical Engineering (IREME), 10, 7, (2016)

[7]

Gapsari F., Soenoko R., Suprapto A., Suprapto W., Bee Wax Propolis Extract as Eco-Friendly Corrosion Inhibitors for 304SS in Sulfuric Acid, International Journal of Corrosion, 2015, pp. 1-10, (2015)

[8]

Suprapto W., Soenoko R., Gapsari F., Comparation of the analytical and experimental models of 304SS corrosion rate in 0.5 m H2SS4 with bee wax propolis extract, Engineering Review, 38, 2, pp. 182-188, (2018)

[9]

Verma A.R.B., van Ooij W.J., High-temperature batch hot-dip galvanizing. Part 1. General description of coatings formed at 560°C, Surface and Coatings Technology, 89, 1-2, pp. 132-142, (1997)

[10]

Bondareva O., Study of the Temperature Effect on the Structure and Thickness of Hot-Dip Zinc Coatings on Fixing Products, Applied Mechanics and Materials, 698, pp. 355-359, (2014)

← 1 2 3 →