Corrosion and Wear Behavior of Impregnated Graphite under Ceramic Pairing

被引：0

作者：

Song W. ^{[1
]}

Li K. ^{[1
]}

Ding X. ^{[1
]}

Ma R. ^{[1
]}

Chen H. ^{[1
]}

机构：

[1] College of Petrochemical Industry, Lanzhou University of Technology, Gansu, Lanzhou

来源：

Mocaxue Xuebao/Tribology | 2024年 / 44卷 / 06期

关键词：

electrochemical corrosion; friction and wear; impregnated graphite; transfer film; wear mechanism;

D O I：

10.16078/j.tribology.2023114

中图分类号：

学科分类号：

摘要：

The friction and corrosion characteristics of impregnated graphite in different media environments were studied by using scanning electron microscope and laser confocal microscope to respectively characterize the surface wear morphology, contact zone wear contour and wear volume. Analyzed the open circuit potential, polarization curve, electrochemical impedance map, and some key parameters related electrochemical impedance in deionized water and seawater, the friction and wear surface properties and mechanism of graphite impregnated paired with two kinds of ceramic dual balls were evaluated and analyzed. The results showed that the self-corrosion current density was lower, the capacitance arc was larger and phase angle was higher, the polarization resistance values were larger, when impregnated graphite was matched with ceramic ball Si3N4, and the impregnated graphite matched with ceramic ball Si3N4 exhibit a characteristic of better corrosion resistance and wear resistance. With the normal load increased, the open circuit potential showed a tendency to move in a negative direction, indicating that the corrosion resistance of graphite contact zone was enhanced. There was obvious furrow phenomenon on the surface of graphite in deionized water, and the wear mechanism was manifested as friction wear. The corrosion products and abrasive debris in the process of graphite wear and corrosion under seawater media formed a transfer film on the contact surface, and the contact surface morphology showed relatively smooth. During friction and corrosion process, the wear volume and dissipated energy in the friction process showed positively correlated with the increase of the normal load, while the wear rate showed negatively correlated with the increase of the normal load. The phenomenon of adhesion showed more obvious in seawater on the graphite contact surface, accompanied by abrasive wear and slight oxidation wear. The contact area in deionized water performed mainly abrasive wear, accompanied by slight adhesive wear and fatigue wear. © 2024 Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences. All rights reserved.

引用

页码：775 / 788

页数：13

共 27 条

[11] Yadav S, Gangwar S, Yadav P C, Et al., Mechanical and corrosion behavior of SiC/Graphite/ZrO2 hybrid reinforced aluminum-based composites for marine environment, Surface Topographymetrology and Properties, 9, 4, (2021)
[12] Wang Jianlei, Zhang Chen, Wang Xiaohu, Et al., Study on wear mechanism of mechanical seal of turbopump of liquid rocket engine impregnated with graphite in N2O4 environment, Journal of Mechanical Engineering, 55, 7, pp. 119-127, (2019)
[13] Yuxuan Xu, Chuanjun Tu, Yanli Liu, Et al., Superior tribology property of zinc phosphate impregnated graphite block at high-temperature oxidative friction[J], Carbon Letters, 32, 5, pp. 1365-1376, (2022)
[14] Jun Zhao, Qingzhan Li, Shuangxi Li, Et al., Influence of a carbon-based tribofilm induced by the friction temperature on the tribological properties of impregnated graphite sliding against a cemented carbide[J], Friction, 9, 4, pp. 686-696, (2021)
[15] Yan Yutao, Li Xuejuan, Hu Guangyang, Et al., Friction and wear behavior and prediction of graphite sealing material at high temperature, Journal of Aerospace Power, 29, 2, pp. 314-320, (2014)
[16] Li Yupeng, Zhu Xiaopeng, Wang Weiguang, Et al., Tribological behaviors of silver impregnated graphite under diffeerent loads in water lubrication conditions, Carbon, 3, pp. 3-9, (2022)
[17] Hongqin Ding, Shuyun Jiang, Comparative study on tribological properties of isostatic pressing graphite and carbon graphite under dry friction and water lubrication conditions[J], Journal of Southeast University (English Edition), 36, 3, pp. 273-277, (2020)
[18] Fei Guo, Tian Yu, Ying Liu, Et al., Ultralow friction between cemented carbide and graphite in water using three-step ring-on-ring friction test[J], Wear, pp. 54-64, (2016)
[19] Yan Wang, Lei Zhang, Hongfei Zhai, Et al., Tribological behavior of Cu-15Ni-8Sn/graphite under sea water, distilled water and dry-sliding conditions[J], Journal of Central South University, 26, 10, pp. 2623-2633, (2019)
[20] Hongming Wei, Jianpeng Zou, Gong Yurong, Et al., Friction and wear behavior of copper/graphite/Ti2SnC composites fabricated by spark plasma sintering (SPS)[J], Wear, pp. 512-513, (2023)

← 1 2 3 →