Tribological Properties of MoS2-Ti Self-lubricating Composite Film at High Temperature

被引：0
作者：
Liu Y. [1 ]
Su F.-H. [1 ]
Sun J.-F. [1 ]
Li Z.-J. [2 ]
Liu Y.-F. [2 ]
机构：
[1] School of Mechanical and Automotive Engineering, South China University of Technology, Guangzhou
[2] School of Electromechanical Engineering, Guangzhou Railway Polytechnic, Guangzhou
来源：
Surface Technology | 2022年 / 51卷 / 02期
基金：
中国国家自然科学基金;
关键词：
high temperature; magnetron sputtering; MoS[!sub]2[!/sub]-Ti composite films; tribological properties; wear mechanism;
D O I：
10.16490/j.cnki.issn.1001-3660.2022.02.002
中图分类号：
学科分类号：
摘要：
This paper aims to explore the effect of Ti content on the tribological properties of MoS2-Ti composite films at high temperature, and prepare MoS2-Ti self-lubricating composite film with good friction properties at high temperature. The MoS2-Ti composite films with different Ti contents were deposited by radio frequency and direct-current dual-target co-sputtering techniques. The effects of Ti content on the microstructures, mechanical properties and tribological behaviors at high temperature of the MoS2-Ti composite films were investigated. The composition, crystal phase structure and microstructure of the films were analyzed by energy dispersive spectroscopy (EDS), X-ray diffraction (XRD) and scanning electron microscopy (SEM). A microhardness tester was applied to evaluate the mechanical properties of the MoS2-Ti composite films. UMT-TriboLab tribotest was employed to evaluate the tribological properties of MoS2-Ti composite films. Raman spectroscopy and X-ray photoelectron spectroscopy (XPS) were used to further analyze the wear surface of the films and the composition of the transfer films on the counterparts. The results showed that Ti doping promoted the growth of the MoS2-Ti composite films in the preferred orientation of (002) crystal plane, and improved the density of the film. The hardness of the film increased from 70HV to 350HV as Ti doping into MoS2. The tribological properties of the MoS2-Ti composite films at high temperature increased firstly and then decreased with the increase of Ti content, and the MoS2-Ti composite films with Ti content of 6.81at.% possessed the best tribological properties. By analyzing the composition of the transfer film, it was found that the wear resistance of the MoS2-Ti composite films with Ti content of 13.51at.% began to decline at 300 ℃ due to more oxides generated during the sliding process. The tribological properties of the MoS2-Ti composite films at high temperature were greatly affected by the Ti content, and appropriate Ti doping could significantly improve the tribological properties of the MoS2 films at high temperature in atmospheric environment. © 2022, Chongqing Wujiu Periodicals Press. All rights reserved.
引用
收藏
页码：20 / 28
页数：8
相关论文
共 30 条
[1]  
DICKINSON R G, PAULING L., The Crystal Structure of Molybdenite, Journal of the American Chemical Society, 45, 6, pp. 1466-1471, (1923)
[2]  
ZHAO Jin-long, DENG Jian-xin, YAN Pei, Preparation of MoS2/Zr Composite Coated Tool and Its Cutting Perfo-rmance, China Mechanical Engineering, 19, 21, pp. 2524-2527, (2008)
[3]  
LIBORIO M S, PRAXEDES G B, LIMA L L F, Et al., Surface Modification of M2 Steel by Combination of Cathodic Cage Plasma Deposition and Magnetron Sputtered MoS2-TiN Multilayer Coatings, Surface and Coatings Technology, 384, (2020)
[4]  
LI Yong-liang, KIM S., Microstructural and Tribological Behavior of TiAlN/MoS2-Ti Coatings, Rare Metals, 25, 4, pp. 326-330, (2006)
[5]  
WANG Jun-an, YU De-yang, OUYANG Jin-lin, Study on the Mechanism of Lubrication Degradation and Failure of MoS2 Sputtered Films Stored in the Moist Air, Tribo-logy, 14, 1, pp. 25-32, (1994)
[6]  
ZHOU Hui, WEN Qing-ping, ZHENG Jun, Et al., The Effect of Ti Content on the Structural and Mechanical Properties of MoS2-Ti Composite Coatings Deposited by Unbalanced Magnetron Sputtering System, Physics Procedia, 18, pp. 234-239, (2011)
[7]  
DING X Z, ZENG X T, HE X Y, Et al., Tribological Properties of Cr-and Ti-Doped MoS2 Composite Coatings under Different Humidity Atmosphere, Surface and Coatings Technology, 205, 1, pp. 224-231, (2010)
[8]  
SUN Jian-rong, LI Chang-sheng, TANG Hua, Et al., Microstructures and Tribological Property of Magnetron Sputtered MoS2/W Coatings, Chinese Journal of Vacuum Science and Technology, 33, 2, pp. 171-175, (2013)
[9]  
OU Wen-min, WEI Chun-bei, DAI Ming-jiang, Et al., Tribological Properties of MoS2-Zr Composite Films, Surface Technology, 46, 1, pp. 93-99, (2017)
[10]  
ARSLAN E, TOTIK Y, BAYRAK O, Et al., High Temperature Friction and Wear Behavior of MoS2/Nb Coating in Ambient Air, Journal of Coatings Technology and Research, 7, 1, pp. 131-137, (2009)
123