Hot deformation behavior and processing maps of iron-nickel based superalloy

被引:0
|
作者
Fazilatpanah, H. [1 ]
Jahangiri, M.R. [2 ]
Khodabandeh, A.R. [1 ]
机构
[1] Department of Materials Engineering, Tehran Science and Research Branch, Islamic Azad University, TEHRAN, Iran
[2] Niroo Reseaech Institute, TEHRAN,14686, Iran
来源
Materialwissenschaft und Werkstofftechnik | 2019年 / 50卷 / 11期
关键词
Plastic flow - Activation energy - Dynamic recrystallization - Iron alloys - Nickel alloys - Compression testing - Nickel - Hot working - Strain rate - Constitutive equations;
D O I
10.1002/mawe.201900019
中图分类号
学科分类号
摘要
Hot deformation behavior of iron-nickel based superalloy (multimet N-155) was investigated by hot compression tests, carried out in the deformation temperature of 850 °C–1150 °C with strain rates of 0.001–0.1 s−1. The results showed that during the hot deformation of the alloy, under the same temperature, the flow stress rises with the increase of strain rate. At the same strain rate, the flow stress decreases with the increase of the temperature. The constitutive equations of the alloy that describe the flow stress as a function of strain rate and deformation temperature were established and the calculated apparent activation energy was 584.996 Kj/mol. The results of metallographic analysis showed that the amount of dynamic recrystallization in the peak efficiency domain is higher than the other domains. The results also showed that by increase of deformation temperature and/or decrease of strain rate, the volume fraction of dynamic recrystallization increases. Processing maps under different strains were constructed for evaluation of flow instability regime and optimization of processing parameters. The optimum hot working window for alloy was obtained at the temperature range of 925 °C–1050 °C and strain rate of 0.001–0.003 s−1, with peak efficiency of 28 %. © 2019 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim
引用
收藏
页码:1407 / 1417
相关论文
共 50 条
  • [21] Cyclic Oxidation and Hot Corrosion Behavior of Nickel-Iron-Based Superalloy
    Chellaganesh, D.
    Khan, M. Adam
    Jappes, J. T. Winowlin
    Sathiyanarayanan, S.
    HIGH TEMPERATURE MATERIALS AND PROCESSES, 2018, 37 (02) : 173 - 180
  • [22] Hot deformation behavior and processing map of a typical Ni-based superalloy
    Wen, Dong-Xu
    Lin, Y. C.
    Li, Hong-Bin
    Chen, Xiao-Min
    Deng, Jiao
    Li, Lei-Ting
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2014, 591 : 183 - 192
  • [23] Cast Structure in Alloy A286, an Iron-Nickel Based Superalloy
    Frisk, Robin
    Andersson, Nils A., I
    Rogberg, Bo
    METALS, 2019, 9 (06)
  • [24] Hot Deformation Behavior of Nickel-Based Superalloy GH4720Li
    Qu Jing-long
    Bi Zhong-nan
    Du Jin-hui
    Wang Min-qing
    Wang Qing-zeng
    Zhang Ji
    JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL, 2011, 18 (10) : 59 - 65
  • [25] Hot Deformation Behavior of Nickel-Based Superalloy GH4720Li
    Jing-long Qu
    Zhong-nan Bi
    Jin-hui Du
    Min-qing Wang
    Qing-zeng Wang
    Ji Zhang
    Journal of Iron and Steel Research International, 2011, 18 : 59 - 65
  • [26] Dynamic recrystallization behavior of a γ′-hardened nickel-based superalloy during hot deformation
    Zhang, Hongbin
    Zhang, Kaifeng
    Jiang, Shaosong
    Zhou, Haiping
    Zhao, Changhong
    Yang, Xiaoli
    JOURNAL OF ALLOYS AND COMPOUNDS, 2015, 623 : 374 - 385
  • [27] Dynamic recrystallization behavior of a typical nickel-based superalloy during hot deformation
    Chen, Xiao-Min
    Lin, Y. C.
    Wen, Dong-Xu
    Zhang, Jin-Long
    He, Min
    MATERIALS & DESIGN, 2014, 57 : 568 - 577
  • [28] Hot Deformation Behavior of Nickel-Based Superalloy GH4720Li
    QU Jing-long 1
    2.Special Steel Multi-Division
    Journal of Iron and Steel Research(International), 2011, 18 (10) : 59 - 65
  • [29] Hot Deformation Behavior of a New Type Nickel-Based P/M Superalloy
    Wu Kai
    Liu Guoquan
    Hu Benfu
    Li Feng
    Zhang Yiwen
    Tao Yu
    Liu Jiantao
    RARE METAL MATERIALS AND ENGINEERING, 2011, 40 (04) : 645 - 649
  • [30] Hot Deformation Behavior and Hot Processing Map of GH2907 Superalloy
    Chen Yizhe
    Pang Yuhua
    Wang Jianguo
    Liu Dong
    Wang Jianyan
    RARE METAL MATERIALS AND ENGINEERING, 2020, 49 (09) : 2956 - 2965