Microstructure and mechanical properties of AZ31Mg/2A12Al laminated composites interface fabricated by explosive welding

被引：0
|
作者：
Wang X. [1 ]
Yang D. [1 ]
Li X. [1 ]
Wang L. [1 ]
Wang K. [1 ]
机构：
[1] Key Laboratory of Controlled Arc Intelligent Additive Manufacturing Technology, Ministry of Industry and Information Technology, Nanjing
来源：
Hanjie Xuebao/Transactions of the China Welding Institution | 2021年 / 42卷 / 05期
关键词：
2A12; AZ31; Explosive welding; Mechanical properties; Microstructure;
D O I：
10.12073/j.hjxb.20201009001
中图分类号：
学科分类号：
摘要：
To compound aluminum alloy plate on the magnesium alloy plate is of great significance to broaden the application range of magnesium alloy. The compounding process test of magnesium alloy plate and aluminum alloy plate was carried out by explosive welding, and the magnesium alloy and aluminum alloy composite plate was fabricated by explosive welding. The optical microscope (OM) and scanning electron microscope (SEM) were used to observe and study the micro-morphology of the bonding interface of the composite board, and the formation process of the interface was analyzed. The hardness and shear strength at the bonding interface of the composite board were measured using a microhardness tester and a shear test machine. The results showed that the melting zone of the composite plate interface fabricated by explosive welding occurred solidified melts, and the structure was a mixture of Al3Mg2 and Al12Mg17 intermetallic compounds. The hardness of the melting zone was 126 HV, which was significantly higher than the substrate hardness (Al alloy 110 HV, Mg alloy 70 HV). There were differences in the shear strength of the specimens in the same sampling direction: the shear strength of the specimens cut along X axis shown a trend of first increasing and then decreasing, and the average value of the shear strength were 112.3 MPa (vertical to the explosion direction) and 87.0 MPa (parallel to the explosion direction); The shear strength of the specimens in the Y-axis direction was basically equivalent, which the value of the shear strength in average were 56.5 MPa (vertical to the explosion direction) and 61.0 MPa (parallel to the explosion direction). Copyright © 2021 Transactions of the China Welding Institution. All rights reserved.
引用
收藏
页码：14 / 17
页数：3
相关论文
共 9 条
  • [1] Zhang Wenyu, The research present situation and application progress of corrosion resistant magnesium alloy, Total Corrosion Control, 33, 1, pp. 6-10, (2019)
  • [2] Sato Y S, Park S H C, Michiuchi M, Et al., Constitutional liquation during dissimilar friction stir welding of Al and Mg alloys, Scripta Materialia, 50, 9, pp. 1233-1236, (2004)
  • [3] Zeng X Y, Wang Y X, Li X Q, Et al., Effect of inert gas-shielding on the interface and mechanical properties of Mg/Al explosive welding composite plate, Journal of Manufacturing Processes, 45, 7, pp. 166-175, (2019)
  • [4] Fang Zhongxing, Shi Changgen, Feng Ke, Et al., Explosive welding experiment and property test of TA2-1060-TA2 cladding plate, Transactions of the China Welding Institution, 40, 9, pp. 93-98, (2019)
  • [5] Yang Ming, Ma Honghao, Shen Zhaowu, Et al., Study on explosive welding for manufacturing meshing bonding interface of CuCrZr to 316L stainless steel, Fusion Engineering and Design, 143, pp. 106-114, (2019)
  • [6] Zeng Xiangyu, Li Xiaojie, Wang Xiaohong, Et al., Formation and development of explosive welding wave interface, Rare Metal Materials and Engineering, 49, 6, pp. 1977-1983, (2020)
  • [7] Pual Henryk, Maj Lukasz, Prazmowski Mariusz, Et al., Microstructure and mechanical properties of multi-layered Al/Ti composites produced by explosive welding, Procedia Manufacturing, 15, pp. 1391-1398, (2018)
  • [8] Shi Qianru, Wu Weigang, Ding Xu, Et al., Study on microstructure and mechanical properties of AZ31Mg/5052Al explosive composite plate, Hot Working Technology, 47, 18, pp. 93-95, (2018)
  • [9] Gladkovsky S V, Kuteneva S V, Sergeev S N, Et al., Microstructure and mechanical properties of sandwich copper/steel composites produced by explosive welding, Materials Characterization, 154, pp. 294-303, (2019)
1