Microwave absorbing properties and magnetic properties of different carbon nanotubes

被引：0
作者：
GUI XuChun WANG KunLin WEI JinQuan L RuiTao SHU QinKe JIA Yi WANG Chen ZHU HongWei WU DeHai Key Laboratory for Advanced Manufacturing by Materials Processing Technology Department of Mechanical Engineering Tsinghua University Beijing China Department of Materials Science and Engineering Tsinghua University Beijing China [1 ,1 ,1 ,2 ,1 ,1 ,2 ,1 ,11 ,100084 ,2 ,100084 ]
机构：
来源：
Science in China(Series E:Technological Sciences) | 2009年 / 01期
关键词：
carbon nanotubes; microwave absorbing properties; magnetic properties;
D O I：
暂无
中图分类号：
TB383.1 [];
学科分类号：
070205 ; 080501 ; 1406 ;
摘要：
The microwave absorbing properties and magnetic properties of as-grown Fe-filled carbon nanotubes (CNTs), annealed Fe-filled CNTs, and multi-walled CNTs were studied. Vibrating sample magnetometer results showed that the annealed Fe-filled CNTs have the weakest coercivity and strongest saturation magnetization among the three types CNTs, due to the presence of more ferromagnetic α-Fe nanowires. After annealing, the values increased to 291.0 Oe and 28.0 emu/g and the samples showed excellent microwave absorbing properties. The reflection loss was over 5 dB between 11.6 GHz and 18 GHz with a maximum value of 10.8 dB for annealed Fe-filled CNTs (1.1 wt%)/epoxy composite.
引用
收藏
页码：227 / 231
页数：5
相关论文
共 6 条
[1]   Improved filling rate and enhanced magnetic properties of Fe-filled carbon nanotubes by annealing and magnetic separation [J].
Gui, Xuchun ;
Wei, Jinquan ;
Wang, Kunlin ;
Wang, Wenxiang ;
Lv, Ruitao ;
Chang, Jianguo ;
Kang, Feiyu ;
Gu, Jialin ;
Wu, Dehai .
MATERIALS RESEARCH BULLETIN, 2008, 43 (12) :3441-3446
[2]   Synthesis of Fe-filled thin-walled carbon nanotubes with high filling ratio by using dichlorobenzene as precursor [J].
Wang, Wenxiang ;
Wang, Kunlin ;
Lv, Ruitao ;
Wei, Jinquan ;
Zhang, Xianfeng ;
Kang, Feiyu ;
Chang, Jianguo ;
Shu, Qinke ;
Wang, Yuquan ;
Wu, Dehai .
CARBON, 2007, 45 (05) :1127-1129
[3]   Investigation of the microwave-absorbing properties of Fe-filled carbon nanotubes [J].
Lin, Haiyan ;
Zhu, Hong ;
Guo, Hongfan ;
Yu, Liufang .
MATERIALS LETTERS, 2007, 61 (16) :3547-3550
[4]  
The complex permittivity of multi-walled carbon nanotube–polystyrene composite films in X-band[J] . P.C.P. Watts,D.R. Ponnampalam,W.K. Hsu,A. Barnes,B. Chambers.Chemical Physics Letters . 2003 (5)
[5]  
Rapid growth of well-aligned carbon nanotube arrays[J] . Xianfeng Zhang,Anyuan Cao,Bingqing Wei,Yanhui Li,Jinquan Wei,Cailu Xu,Dehai Wu.Chemical Physics Letters . 2002 (3)
[6]  
The 500 MHz to 5.50 GHz complex permittivity spectra of single-wall carbon nanotube-loaded polymer composites[J] . C.A. Grimes,C. Mungle,D. Kouzoudis,S. Fang,P.C. Eklund.Chemical Physics Letters . 2000 (5)
1