Inkjet-Printed Flexible and Transparent Ti3C2Tx/TiO2 Composite Films: A Strategy for Photoelectrically Controllable Photocatalytic Degradation

The 2D Ti(3)C2T(x) MXene has a large specific surface area, abundant functional groups, and low work function, which has potential in the field of photocatalytic materials. However, the manufacturing of controllable films with high photocatalytic properties and desirable transmittance is a challenging task. Herein, low-cost, large-scale, and rapid preparation of Ti3C2Tx/TiO2 flexible composite films have been successfully prepared by inkjet printing technology, which can be applied in complex and special environments, as well as in photoelectrically controllable places for photocatalytic performance. With the increase of the anatase TiO2, the transmittance of Ti3C2Tx/TiO2 films increases from 55.37% to 73.27% at 780 nm, corresponding to the square resistance of 1.112-206.496 k Omega sq(-1) and the figure of merit of 0.48-0.005. When the amount of anatase TiO2 is 15%, the film has the best photocatalytic effect on methylene blue (MB) dye, reaching 68.94%. After five cycles of testing, the degradation efficiency of MB dye decreases by only 5.68%, showing that the film has good cycling stability. This work provides a new research direction for photoelectrically controllable photocatalytic degradation in complex and special environments.