Short-Term Oxidation in HT-SEM of the Pt-Containing TROPEA Single Crystal Ni-Based Superalloy from 680 to 1000 °C

被引:2
作者
Mathieu, S. [1 ]
Podor, R. [2 ]
Emo, M. [1 ]
Hunault, L. [3 ]
Vilasi, M. [1 ]
Cormier, J. [4 ]
Pedraza, F. [3 ]
机构
[1] Univ Lorraine, CNRS, IJL, Nancy, France
[2] Univ Montpellier, CNRS, CEA, ICSM,ENSCM, Site Marcoule, Bagnols Sur Ceze, France
[3] La Rochelle Univ, LaSIE, La Rochelle, France
[4] Inst PPRIME, ISAE ENSMA, UPR CNRS 3346, F-86961 Futuroscope, Chasseneuil Du, France
关键词
Nickel-based superalloy; Oxidation; In situ observation; HOT CORROSION; CYCLIC OXIDATION; NICKEL; BEHAVIOR; MECHANISM;
D O I
10.1007/s11085-024-10272-9
中图分类号
TF [冶金工业];
学科分类号
0806 ;
摘要
Short-time oxidation exposures of the Ni-based TROPEA single crystal superalloy was implemented to determine the nature and quantities of transient oxides in the 680-1000 degrees C temperature range. Experiments were carried out in situ in the SEM with reduced air pressure (150 Pa, P-O2 similar to 31.5 Pa) compared to atmospheric conditions (10(5) Pa, P-O2 similar to 2.1 10(4) Pa). TEM characterization after oxidation showed the complexity of the oxidation products developed. Aluminum underwent internal oxidation between 680 and 1000 degrees C. During the limited duration of oxidation, the TROPEA alloy only formed a continuous alumina layer at 1000 degrees C. At 680 and 850 degrees C, the low diffusion rate and small amount of Al in the Ni-based single crystal led to the formation of a significant amount of transient oxides such as (Ni,Co)O, compared to the desired chromia or alumina protective oxides. The lower the temperature, the smaller the size of the internal Al2O3 precipitates and the larger the transient oxide amount, which would lower the resistance of TROPEA to Type II hot corrosion. In contrast after a transient period shorter than 22 h, during which multiple transient oxide developed, the oxidation resistance would be ensured at 1000 degrees C by the formation of a continuous Al2O3 scale.
引用
收藏
页码:1211 / 1223
页数:13
相关论文
共 29 条
[1]  
Barin I., 1991, Thermochemical Properties of Inorganic Substances, V2nd ed.
[2]   Effect of stress state and simultaneous hot corrosion on the crack propagation and fatigue life of single crystal superalloy CMSX-4 [J].
Brooking, L. ;
Gray, S. ;
Sumner, J. ;
Nicholls, J. R. ;
Marchant, G. ;
Simms, N. J. .
INTERNATIONAL JOURNAL OF FATIGUE, 2018, 116 :106-117
[3]   Role of tantalum in the hot corrosion of a Ni-base single crystal superalloy [J].
Chang, J. X. ;
Wang, D. ;
Liu, T. ;
Zhang, G. ;
Lou, L. H. ;
Zhang, J. .
CORROSION SCIENCE, 2015, 98 :585-591
[4]   A GASEOUS DETECTOR DEVICE FOR AN ENVIRONMENTAL SEM [J].
DANILATOS, GD .
MICRON AND MICROSCOPICA ACTA, 1983, 14 (04) :307-318
[5]   MECHANISM OF BENEFICIAL EFFECT OF TANTALUM IN HOT CORROSION OF NICKEL-BASE SUPERALLOYS [J].
FRYBURG, GC ;
STEARNS, CA ;
KOHL, FJ .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1977, 124 (07) :1147-1148
[6]   Effects of platinum on the interdiffusion and oxidation behavior of Ni-Al-based alloys [J].
Gleeson, B ;
Wang, W ;
Hayashi, S ;
Sordelet, D .
HIGH TEMPERATURE CORROSION AND PROTECTION OF MATERIALS 6, PRT 1 AND 2, PROCEEDINGS, 2004, 461-464 :213-222
[7]   MECHANISMS FOR HOT CORROSION OF NICKEL-BASE ALLOYS [J].
GOEBEL, JA ;
PETTIT, FS ;
GOWARD, GW .
METALLURGICAL TRANSACTIONS, 1973, 4 (01) :261-278
[8]   INTERNAL OXIDATION OF AG-IN ALLOYS - STRESS RELIEF AND THE INFLUENCE OF IMPOSED STRAIN [J].
GURUSWAMY, S ;
PARK, SM ;
HIRTH, JP ;
RAPP, RA .
OXIDATION OF METALS, 1986, 26 (1-2) :77-100
[9]   Comparison of the cyclic oxidation behavior of β-NiAl, β-NiPtAl and γ-γ′ NiPtAl coatings on various superalloys [J].
Haynes, J. A. ;
Pint, B. A. ;
Zhang, Y. ;
Wright, I. G. .
SURFACE & COATINGS TECHNOLOGY, 2007, 202 (4-7) :730-734
[10]   Examination of the platinum effect on the oxidation behavior of nickel-aluminide coatings [J].
Hou, P. Y. ;
Tolpygo, V. K. .
SURFACE & COATINGS TECHNOLOGY, 2007, 202 (4-7) :623-627