The effects of the band gap and defects in silicon nitride on the carrier lifetime and the transmittance in c-Si solar cells

被引:25
作者
Jung, Sungwook [1 ,2 ]
Gong, Deayoung [2 ]
Yi, Junsin [1 ,2 ]
机构
[1] Sungkyunkwan Univ, Dept Energy Sci, Suwon 440746, South Korea
[2] Sungkyunkwan Univ, Sch Informat & Commun Engn, Suwon 440746, South Korea
关键词
Solar cell; Antireflection coating; Passivation; Band gap; Defect states; TEMPERATURE SURFACE PASSIVATION; PECVD; RECOMBINATION; LUMINESCENCE; DEPOSITION; FILMS; BULK;
D O I
10.1016/j.solmat.2010.09.014
中图分类号
TE [石油、天然气工业]; TK [能源与动力工程];
学科分类号
0807 ; 0820 ;
摘要
In this paper, silicon nitride thin films with different silane and ammonia gas ratios were deposited and characterized for the antireflection and passivation layer of high efficiency single crystalline silicon solar cells. An increase in the transmittance and a recombination decrease using an effective antireflection and passivation layer can be enhanced by an optimized SiN(x) film in order to attain higher solar cell efficiencies. As the flow rate of the ammonia gas increased, the refractive index decreased and the band gap increased. Consequently, the transmittance increased due to the higher band gap and the decrease of the defect states, which existed for the 1.68 and 1.80 eV in the SiN(x) films. The interface trap density found in silicon can be reduced down to 1.0 x 10(10) cm(-2) eV(-1) for the SiN(x) layer deposited under the optimized silane to ammonia gas ratio. Reduction in the carrier lifetime of the SiN(x) films deposited using a higher NH(3)/SiH(4) flow ratio was caused by the increase of the interface traps and the defect states in/on the interface between the SiN(x) and the silicon wafer. Silicon and nitrogen rich films are not suitable for generating both higher carrier lifetimes and transmittance. An improvement in the single c-Si solar cell parameters was observed for the cells with an optimal SiN(x) layer, as compared to those with non-optimal SiN(x) layers. These results indicate that the band gap and the defect states of the SiN(x) films should be carefully controlled in order to obtain the maximum efficiency for c-Si solar cells. (C) 2010 Elsevier B.V. All rights reserved.
引用
收藏
页码:546 / 550
页数:5
相关论文
共 24 条
  • [1] Aberle AG, 1997, PROG PHOTOVOLTAICS, V5, P29, DOI 10.1002/(SICI)1099-159X(199701/02)5:1<29::AID-PIP149>3.0.CO
  • [2] 2-M
  • [3] Spectroscopic ellipsometry for in-line monitoring of silicon nitrides
    Cook, CS
    Daly, T
    Liu, R
    Canonico, M
    Xie, Q
    Gregory, RB
    Zollner, S
    [J]. THIN SOLID FILMS, 2004, 455 : 794 - 797
  • [4] DANGLING BONDS IN MEMORY-QUALITY SILICON-NITRIDE FILMS
    FUJITA, S
    SASAKI, A
    [J]. JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1985, 132 (02) : 398 - 402
  • [5] High-Efficiency Crystalline Silicon Solar Cells
    Glunz, S. W.
    [J]. ADVANCES IN OPTOELECTRONICS, 2007, 2007
  • [6] Photovoltaic materials, history, status and outlook
    Goetzberger, A
    Hebling, C
    Schock, HW
    [J]. MATERIALS SCIENCE & ENGINEERING R-REPORTS, 2003, 40 (01) : 1 - 46
  • [7] Goetzberger A., 1998, CRYSTALLINE SILICON, P87
  • [8] Solar photovoltaics R&D at the tipping point: A 2005 technology overview
    Kazmerski, LL
    [J]. JOURNAL OF ELECTRON SPECTROSCOPY AND RELATED PHENOMENA, 2006, 150 (2-3) : 105 - 135
  • [9] Surface recombination velocity of phosphorus-diffused silicon solar cell emitters passivated with plasma enhanced chemical vapor deposited silicon nitride and thermal silicon oxide
    Kerr, MJ
    Schmidt, J
    Cuevas, A
    Bultman, JH
    [J]. JOURNAL OF APPLIED PHYSICS, 2001, 89 (07) : 3821 - 3826
  • [10] Low temperature surface passivation for silicon solar cells
    Leguijt, C
    Lolgen, P
    Eikelboom, JA
    Weeber, AW
    Schuurmans, FM
    Sinke, WC
    Alkemade, PFA
    Sarro, PM
    Maree, CHM
    Verhoef, LA
    [J]. SOLAR ENERGY MATERIALS AND SOLAR CELLS, 1996, 40 (04) : 297 - 345