Effect of Corrosion Environment on Mechanical Behavior of 5083/6005A Welded Joints

被引:0
作者
Wu, Hailiang [1 ]
Chen, Yuqiang [1 ]
Lu, Dingding [1 ]
He, Guanqiang [2 ]
机构
[1] Hunan Univ Sci & Technol, Hunan Engn Res Ctr Forming Technol & Damage Resist, Xiangtan 411201, Peoples R China
[2] Zhuzhou CRRC Times Elect Co Ltd, Zhuzhou 412001, Peoples R China
基金
中国国家自然科学基金; 中国博士后科学基金;
关键词
aluminum alloy welded joint; corrosive medium; stress corrosion; corrosion fatigue life; corrosion mechanism; ALUMINUM-ALLOY; ATMOSPHERIC CORROSION; RESISTANCE; MICROSTRUCTURE; MORPHOLOGY; INDUSTRIAL; CRACKING; TIME;
D O I
10.3390/met14080925
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The corrosion fatigue behavior of welded joints is a critical concern in the transportation industry, which shortens their service life. In this paper, the corrosion damage of 5083/6005A welded joints exposed to different conditions (3.5% NaCl + 0.01 mol/L NaHSO3, 3.5% NaCl, 0.6 mol/L NaHSO3, and 3.5% NaCl + 0.01 mol/L NaHSO3-75 MPa) was investigated by using tensile and fatigue tests, polarization curves, scanning electron microscopy (SEM), and X-ray photoelectron spectroscopy (XPS). The findings indicate that elongation and fatigue life were most adversely affected by exposure to 3.5% NaCl + 0.01 mol/L NaHSO3-75 MPa. This was followed by the exposure to 3.5% NaCl + 0.01 mol/L NaHSO3, then 3.5% NaCl, with the mildest effects observed under 0.6 mol/L NaHSO3. The corrosion mechanisms were elucidated and the corrosion model was established through the analysis of corrosion morphologies and corrosion products. The corrosion fatigue fracture model was developed by analyzing the fracture surfaces. These findings provide references for preventing the corrosion-fatigue fractures of 5083/6005A welded joints, extending their service life, and enhancing the operational safety and reliability of trains.
引用
收藏
页数:18
相关论文
共 50 条
  • [41] Effect of precipitate evolution on corrosion behavior of friction stir welded joints of AA2060-T8 alloy
    Meng, Qiang
    Liu, Yang
    Kang, Ju
    Fu, Rui-dong
    Guo, Xiao-yan
    Li, Yi-jun
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2019, 29 (04) : 701 - 709
  • [42] Effect of the Number of Welding Repairs with GTAW on the Mechanical Behavior of AA7020 Aluminum Alloy Welded Joints
    Maya-Johnson, Santiago
    Felipe Santa, Juan
    Mejia, Oscar L.
    Aristizabal, Santiago
    Ospina, Sebastian
    Andrea Cortes, Paula
    Enrique Giraldo, Jorge
    METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE, 2015, 46 (05): : 2332 - 2339
  • [43] Effect of hydrogen on the pitting corrosion of 2205 duplex stainless steel welded joints
    Zheng, Qing
    Zhang, Houwei
    Wang, Dengyun
    Xu, Lining
    Li, Gang
    Qiao, Lijie
    CORROSION ENGINEERING SCIENCE AND TECHNOLOGY, 2024, 59 (02) : 104 - 119
  • [44] Effect of Microstructure Evolution on Corrosion Behavior of Friction Stir Welded Joint for 2195-T8 Alloy
    Hu, B. Y.
    Zhang, H.
    Liu, L. Y.
    Liu, D. B.
    Feng, A. H.
    Chen, D. L.
    CORROSION, 2020, 76 (12) : 1099 - 1108
  • [45] Effect of Interface Morphology on the Mechanical Properties of Friction Stir Welded T-lap Joints of 7075/5083 Aluminum Alloys
    Hao Dinh Duong
    Tra Hung Tran
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2021, 52 (07): : 3023 - 3033
  • [46] Innovative Approach for the Evaluation of the Mechanical Behavior of Dissimilar Welded Joints
    Carone, Simone
    Corigliano, Pasqualino
    Epasto, Gabriella
    Moramarco, Vincenzo
    Palomba, Giulia
    Pappalettera, Giovanni
    Casavola, Caterina
    METALS, 2022, 12 (12)
  • [47] Effect of aging on the corrosion behavior of 6005 Al alloys in 3.5 wt% NaCl aqueous solution
    Li, Wenkai
    Chen, Xia
    Chen, Bin
    JOURNAL OF MATERIALS RESEARCH, 2018, 33 (12) : 1830 - 1838
  • [48] EFFECTS OF LINE ENERGY ON MECHANICAL PROPERTIES, CORROSION AND SHAPE MEMORY BEHAVIOR OF LASER-WELDED NiTinol JOINTS
    Datta, Susmita
    Raza, Mohammad Shahid
    Saha, Partha
    Pratihar, Dilip Kumar
    PROCEEDINGS OF THE ASME 13TH INTERNATIONAL MANUFACTURING SCIENCE AND ENGINEERING CONFERENCE, 2018, VOL 4, 2018,
  • [49] Stress corrosion behavior and microstructure analysis of Al-Zn-Mg-Cu alloys friction stir welded joints under different aging conditions
    Guo, Fuqiang
    Duan, Shuwei
    Pan, Yuzhe
    Wu, Dongting
    Matsuda, Kenji
    Wang, Tao
    Zou, Yong
    CORROSION SCIENCE, 2023, 210
  • [50] Base material location dependence of corrosion response in friction-stir-welded dissimilar 2024-to-5083 aluminum alloy joints
    Niu, Peng-liang
    LI, Wen-ya
    Chen, Yu-hua
    Liu, Qi-peng
    Chen, Dao-lun
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2022, 32 (07) : 2164 - 2176