Electropolishing of 316L Stainless Steel Small-Diameter Tubes: Reduced Surface Roughness and Enhanced Corrosion Resistance

被引:0
作者
Feng, Kai [1 ]
Liu, Chaonan [1 ]
Wang, Yu [1 ]
Wang, Zhenwei [1 ]
机构
[1] Shanghai Inst Technol, Sch Chem & Environm Engn, Shanghai 201418, Peoples R China
关键词
316L stainless steel tubes; corrosion resistance; electropolishing; surface roughness; XPS; GAS; SS;
D O I
10.1007/s11665-024-10090-9
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Semiconductor, pharmaceutical, and food processing industries require highly clean and corrosion-resistant 316L stainless steel pipelines to prevent product contamination and ensure durability. This study employs an optimized electropolishing technique for small-diameter 316L stainless steel tubes, aimed at significantly reducing surface roughness and enhancing corrosion resistance to meet stringent industry standards. A comprehensive examination of the effects of electropolishing parameters-polishing time, current density, and temperature-on surface roughness and morphology was conducted. Optimal conditions were determined to be 105 seconds of polishing time, a current density of 50 A<middle dot>dm(-2), and a temperature of 60 degrees C. Under these conditions, the tube achieves a mirror-like finish with a surface roughness of 0.063 mu m. Corrosion resistance was characterized using electrochemical testing and x-ray photoelectron spectroscopy. The electropolished tube exhibits superior corrosion resistance compared to the mechanically polished tube, which is attributed to its increased thickness and chromium-rich passive film.
引用
收藏
页数:13
相关论文
共 50 条
  • [41] Electrochemical and XPS studies of AISI 316L stainless steel after electropolishing in a magnetic field
    Hryniewicz, T.
    Rokosz, K.
    Rokicki, R.
    CORROSION SCIENCE, 2008, 50 (09) : 2676 - 2681
  • [42] Enhanced the SRB corrosion resistance of 316L stainless steel via adjusting the addition of Cu and Ce elements
    Song, Dazhuo
    Zou, Juntao
    Sun, Lixing
    Zhang, Yipeng
    Zhang, Jiayue
    Liang, Xinhang
    Zhang, Shuqin
    Li, Yunshuai
    Li, Huajun
    Xi, Bo
    Wu, Ze
    Song, Yuchen
    VACUUM, 2024, 224
  • [43] Corrosion resistance of heated 316L stainless steel with CrC coating in PEMFC environment
    Huang, Naibao
    Pei, Lilin
    Liang, Chenghao
    Xu, Lishuang
    Yu, Hong
    Yang, Hui
    2013 INTERNATIONAL CONFERENCE ON MATERIALS FOR RENEWABLE ENERGY AND ENVIRONMENT (ICMREE), VOLS 1-3, 2013, : 419 - 423
  • [44] Enhanced mechanical properties and corrosion resistance of 316L stainless steel by pre-forming a gradient nanostructured surface layer and annealing
    Lei, Y. B.
    Wang, Z. B.
    Zhang, B.
    Luo, Z. P.
    Lu, J.
    Lu, K.
    ACTA MATERIALIA, 2021, 208
  • [45] Corrosion resistance of TiN coated 316L stainless steel in artificial physiological solution
    Braic, M
    Zamfir, S
    Balaceanu, M
    Braic, V
    Pavelescu, G
    Zamfir, A
    Vladescu, A
    JOURNAL OF OPTOELECTRONICS AND ADVANCED MATERIALS, 2003, 5 (02): : 503 - 510
  • [46] Corrosion resistance and biocompatibility of cold-sprayed titanium on 316L stainless steel
    Wathanyu, Kessaraporn
    Tuchinda, Karuna
    Daopiset, Siriporn
    Sirivisoot, Sirinrath
    Surface and Coatings Technology, 2022, 445
  • [47] Corrosion performance of the plasma nitrided 316L stainless steel
    Gil, Linda
    Bruhl, Sonia
    Jimenez, Lorena
    Leon, Ovidio
    Guevara, Rafael
    Staia, Maniana H.
    SURFACE & COATINGS TECHNOLOGY, 2006, 201 (07) : 4424 - 4429
  • [48] Effect of surface passivation on corrosion resistance and antibacterial properties of Cu-bearing 316L stainless steel
    Zhao, Jinlong
    Xu, Dake
    Shahzad, M. Babar
    Kang, Qiang
    Sun, Ying
    Sun, Ziqing
    Zhang, Shuyuan
    Ren, Ling
    Yang, Chunguang
    Yang, Ke
    APPLIED SURFACE SCIENCE, 2016, 386 : 371 - 380
  • [49] Surface Morphology Analysis and Roughness Prediction of 316L Stainless Steel by Selective Laser Melting
    Mu Weihao
    Chen Xuehui
    Zhang Yu
    Huang Lei
    Zhu Darong
    Dong Bichun
    LASER & OPTOELECTRONICS PROGRESS, 2022, 59 (07)
  • [50] Collaborative Optimization of Density and Surface Roughness of 316L Stainless Steel in Selective Laser Melting
    Deng, Yong
    Mao, Zhongfa
    Yang, Nan
    Niu, Xiaodong
    Lu, Xiangdong
    MATERIALS, 2020, 13 (07)