Strontium ferrite oxide (Sr3Fe2O7) 3 Fe 2 O 7 ) decorated TiO2 2 photoanode improves the photo-absorption and photoelectrochemical cell efficiency

被引:1
作者
Panchakhant, Pandhabhatra [1 ]
Wannapop, Surangkana [1 ]
Yana, Janchai [2 ]
Smith, Siwaporn Meejoo [3 ,4 ]
Somdee, Asanee [1 ]
机构
[1] King Mongkuts Univ Technol North Bangkok, Fac Sci Energy & Environm, Rayong Campus, Rayong 21120, Thailand
[2] Chiang Mai Rajabhat Univ, Fac Sci & Technol, Dept Chem, Chiang Mai 50300, Thailand
[3] Mahidol Univ, Ctr Sustainable Energy & Green Mat, Nakhon Pathom 73170, Thailand
[4] Mahidol Univ, Fac Sci, Dept Chem, Nakhon Pathom 73170, Thailand
关键词
Titanium dioxide; Strontium ferrite oxide; Photoelectrochemical cell; Water splitting; WATER; HYDROGEN; ABSORPTION; ELECTRODES; FILMS;
D O I
10.1016/j.ceramint.2024.06.084
中图分类号
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
In this study, a coating of strontium ferrite oxide (SFO), Sr3Fe2O7, on TiO2 demonstrated an enhancement in photoelectrochemical cell (PEC) performance. Pure TiO2 and SFO decorated TiO2 (SFO/TiO2) were synthesized using the hydrothermal method. The concentration of SFO precursor in this study varied between 0.5, 1.0, and 1.5 mmol. Most of the optimized SFO concentration showed the better Applied Bias Photon-to-current Efficiency than the pure TiO2. The structure, chemistry, and surface morphology of TiO2 and SFO/TiO2 materials were investigated using several techniques, including X-ray diffraction, transmission electron microscopy, and energydispersive X-ray spectroscopy. The UV-visible spectra revealed that SFO was able to reduce the energy band gap of pristine TiO2 from 3.09 to 2.55 eV. The photoluminescence spectroscopy displayed that almost SFO/TiO2 materials exhibited the lower recombination time than the pristine TiO2. Moreover, 1.0 mmol of SFO/TiO2 exhibited the highest photocurrent density, at approximately 12.5 mu A/cm2, which was 12 times greater than pure TiO2. The Mott-Schottky analysis revealed the energy band edge of SFO and the TiO2 was well alignment. Therefore, SFO plays a crucial role in improving the photo-absorption efficiency of PEC cell. The enhanced PEC performance was achievable due to the materials' tailored light response.
引用
收藏
页码:32748 / 32754
页数:7
相关论文
共 49 条
[41]   In situ fabrication of nanoporous BiVO4/Bi2S3 nanosheets for enhanced photoelectrochemical water splitting [J].
Wang, Min ;
Wang, Qiming ;
Guo, Peizhi ;
Jiao, Zhengbo .
JOURNAL OF COLLOID AND INTERFACE SCIENCE, 2019, 534 :338-342
[42]   Perovskite Oxide-Based Electrodes for High-Performance Photoelectrochemical Water Splitting [J].
Wang, Wei ;
Xu, Meigui ;
Xu, Xiaomin ;
Zhou, Wei ;
Shao, Zongping .
ANGEWANDTE CHEMIE-INTERNATIONAL EDITION, 2020, 59 (01) :136-152
[43]   Integration of MgAl-layered double hydroxides into TiO2 nanorods as photoanodes for enhanced photoelectrochemical water splitting [J].
Wang, Yanjun ;
Zhang, Zhengyang ;
Wang, Shiwei ;
Han, Minmin .
CATALYSIS COMMUNICATIONS, 2022, 164
[44]   Enhanced visible light absorption of TiO2 nanorod photoanode by NiTiO3 decoration for high-performance photoelectrochemical cells [J].
Wannapop, Surangkana ;
Somdee, Asanee .
CERAMICS INTERNATIONAL, 2020, 46 (16) :25758-25765
[45]   Preparation of GQDs/TiO2 nanotube heterojunction photoanode and its photoelectrochemical performance for water splitting [J].
Xiao, Zhizhong ;
Cheng, Shengye ;
Liao, Wenbo ;
Fan, Dayong ;
Lu, Huidan ;
Liu, Yongping .
INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE, 2022, 17 (08)
[46]   The borophene quantum dots scaffolded TiO2 nanocomposite as an efficient photo electrocatalyst for water splitting application [J].
Yashwanth, H. J. ;
Hareesh, K. ;
Rondiya, Sachin R. ;
Choudhary, Ram J. ;
Dhole, Sanjay D. .
APPLIED SURFACE SCIENCE, 2024, 646
[47]   PEC water splitting using mats of calcined TiO2 rutile nanorods photosensitized by a thin layer of Ni-benzene dicarboxylic acid MOF [J].
You, Sheng-Mu ;
Wang, Tzu-Heng ;
Doong, Ruey-An ;
Millet, Pierre .
ELECTROCHIMICA ACTA, 2021, 393
[48]   Overcoming Charge Collection Limitation at Solid/Liquid Interface by a Controllable Crystal Deficient Overlayer [J].
Zhang, Kan ;
Ravishankar, Sandheep ;
Ma, Ming ;
Veerappan, Ganapathy ;
Bisquert, Juan ;
Fabregat-Santiago, Francisco ;
Park, Jong Hyeok .
ADVANCED ENERGY MATERIALS, 2017, 7 (03)
[49]  
Zhang K, 2016, ADV ENERGY MATER, V6, DOI [10.1002/aenm.201600602, 10.1002/aenm.201600811]