Solid/Molten Na2SO4-Induced Hot Corrosion Behaviors of Mar-M247 Alloy with CVD Aluminide Coatings

被引：0
|
作者：
Hu, Qi [1 ]
Geng, Shujiang [1 ]
Wang, Jinlong [1 ]
Wang, Fuhui [1 ]
Sun, Qingyun [2 ]
Xia, Siyao [2 ]
Wu, Yong [2 ]
机构：
[1] Northeastern Univ, Corros & Protect Ctr, 3-11 Wenhua Rd, Shenyang 110819, Peoples R China
[2] Wuhan Res Inst Mat Protect Co Ltd, CAM, Wuhan 430030, Peoples R China
来源：
HIGH TEMPERATURE CORROSION OF MATERIALS | 2024年 / 101卷 / SUPPL 1期
基金：
国家重点研发计划;
关键词：
Hot corrosion; Na2SO4; Solid/molten; Aluminide coating; CVD; HIGH-TEMPERATURE CORROSION; TURBINE-BLADES; MICROSTRUCTURE; RESISTANCE; MECHANISMS; OXIDATION; PERFORMANCE; DEPOSITION; SULFATE; NA2SO4;
D O I：
10.1007/s11085-024-10315-1
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
Aluminide coatings were prepared by chemical vapor deposition (CVD) method on Ni-based superalloy Mar-M247 to improve the corrosion resistance. The Na2SO4-induced hot corrosion behavior of Mar-M247 with and without aluminide coating was investigated at varying temperatures. The results revealed that the substrate underwent relatively mild corrosion attack at temperatures below the Na2SO4 melting point, but extremely severe corrosion attack above it. The aluminide coating significantly improved the corrosion resistance of the substrate, with the formation of Al2O3 scale during corrosion. The effects of both solid and molten Na2SO4 on hot corrosion resistance of Mar-M247 alloy and its aluminide coating was discussed, as well as the detrimental effect of tungsten on the substrate in 'type I' hot corrosion.
引用
收藏
页码：283 / 307
页数：25
相关论文
共 50 条
  • [31] Improving the Na2SO4-induced corrosion resistance of Ti3AlC2 by pre-oxidation in air
    Lin, Zhijun
    Zhou, Yanchun
    Li, Meishuan
    Wang, Jingyang
    CORROSION SCIENCE, 2006, 48 (10) : 3271 - 3280
  • [32] Na2SO4 deposit-induced hot corrosion of BN-coated α-SiC
    Herweyer, L. A.
    Opila, E. J.
    JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2021, 104 (03) : 1539 - 1553
  • [33] Na2SO4 Induced Hot Corrosion of Aluminized Low Carbon Steel at 700 °C
    Badaruddin, Mohammad
    ADVANCES IN APPLIED MECHANICS AND MATERIALS, 2014, 493 : 761 - 766
  • [34] Comparison of Na2SO4, K2SO4 and Na2SO4-K2SO4 deposit induced hot corrosion of a β-NiAl coating
    Wang, Yaping
    Pillai, Rishi
    Yazhenskikh, Elena
    Frommherz, Martin
    Mueller, Michael
    Quadakkers, Willem Joseph
    Naumenko, Dmitry
    CORROSION SCIENCE, 2022, 198
  • [35] Hot corrosion behavior and mechanism of FGH96 P/M superalloy in molten NaCl–Na2SO4 salts
    He Jiang
    Jian-Xin Dong
    Mai-Cang Zhang
    Lei Zheng
    Zhi-Hao Yao
    Rare Metals, 2019, 38 : 173 - 180
  • [36] Hot corrosion behavior and mechanism of FGH96 P/M superalloy in molten NaCl–Na2SO4 salts
    He Jiang
    Jian-Xin Dong
    Mai-Cang Zhang
    Lei Zheng
    Zhi-Hao Yao
    Rare Metals, 2019, 38 (02) : 173 - 180
  • [37] Hot corrosion mechanism of yttria-stabilized zirconia powder in the presence of molten Na2SO4 + V2O5 salts
    De la Roche, Jhonattan
    Manuel Alvarado-Orozco, Juan
    Toro, Alejandro
    RARE METALS, 2021, 40 (05) : 1307 - 1316
  • [38] Hot Corrosion Behavior of Inconel 625 in Na2SO4 and V2O5 Molten Salt System
    Li, Liang
    Li, Lanfeng
    Zhang, Guofeng
    Xue, Hongdi
    Cui, Maomao
    Wang, Wenxu
    Liu, Dexue
    METALS, 2023, 13 (06)
  • [39] Hot corrosion behavior of a Si-Y co-deposition coating on a Ti2AlNb based alloy in NaCl-Na2SO4 mixture
    Xiang, Jiayi
    Xie, Faqin
    Wu, Xiangqing
    Wang, Shaoqing
    Li, Lang
    SURFACE & COATINGS TECHNOLOGY, 2021, 419
  • [40] Hot corrosion behavior of powder metallurgy Rene95 nickel-based superalloy in molten NaCl-Na2SO4 salts
    Lei Zheng
    Zhang Maicang
    Dong Jianxin
    MATERIALS & DESIGN, 2011, 32 (04): : 1981 - 1989
12345