Hydrological response and crack resistance of polypropylene-fiber reinforced compacted steel slag-bentonite mixtures under wetting-drying cycles

Desiccation-induced cracks in a compacted clay liner significantly deteriorate the hydraulic barrier performance of landfill covers. The present study explores the effects of polypropylene (PP) fiber reinforcement on the hydrological response and crack resistance of compacted steel slag (SS; 90 wt%) - bentonite (10 wt%) mixtures under drying and wetting cycles. Comprehensive tests were conducted to explore the impact of different fiber lengths (6-12 mm) and contents (0-0.4 % wt.%), including hydraulic conductivity tests for measuring the saturated hydraulic conductivity (ks), unconfined-penetration tests for measuring the tensile strength, small-sized plate tests for quantifying crack development, and large-sized bucket tests for studying the hydrological response and crack characteristics. Higher fiber contents and longer fiber lengths increased the ks-value of the specimens. For a 0.3 % fiber content, the tensile strength peaked for the 9-mm fiber. Consistently, the specimen reinforced with the 9-mm fibers exhibited significantly fewer cracks than those reinforced with the 6-mm and 12-mm fibers. It was because the 6-mm fibers had a shorter anchorage length, while the 12-mm fibers tended to agglomerate. The large-sized bucket tests showed that fiber reinforcement limited crack development significantly under wetting and drying cycles, reducing the rainfall infiltration by 40 % and enhancing the soil water retention capacity. Finally, a 0.3 wt% of 9-mm PP was recommended to reinforce the compacted SS-bentonite mixtures.