Hot deformation and dynamic recrystallization of Mg-Gd-Y-Zn-Zr alloy containing high volume fraction 18R-LPSO phase

被引:6
|
作者
Hu, Liqiang [1 ]
Wang, Jianli [1 ]
Zheng, Pengcheng [1 ]
Wang, Ke [1 ]
Wang, Yili [1 ]
Liu, Jiliang [1 ]
Wang, Liying [1 ,2 ]
Wang, Ding [2 ]
Yang, Zhong [1 ]
机构
[1] Xian Technol Univ, Sch Mat Sci & Chem Engn, Xian 710021, Peoples R China
[2] Xian Tianli Clad Met Mat Co Ltd, Xian 710299, Peoples R China
关键词
LPSO; Mg-Gd-Y-Zn-Zr alloy; Dynamic recrystallization; Thermal deformation; Microstructure evolution; MICROSTRUCTURE EVOLUTION; CONSTITUTIVE ANALYSIS; MAGNESIUM ALLOYS; PROCESSING MAP; COMPRESSIVE DEFORMATION; BEHAVIOR; LPSO; STRENGTH; WORKABILITY; PARAMETERS;
D O I
10.1016/j.jallcom.2024.175718
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
The deformation behavior including flow behavior, hot workability and dynamic recrystallization (DRX) mechanism of as-cast Mg-9Gd-3Y-3.75Zn-0.6Zr alloy containing 26.5% volume fraction 18R long-period stacking ordered (LPSO) phase distributed in continuous network morphology were studied by hot compression experiments at deformation condition of 350 degrees C-500 degrees C, 0.01-1 s(-1) strain rate and 0.75 true strain. The influence of deformation conditions on the microstructural evolution was analyzed by using optical microscopy (OM), scanning electron microscope (SEM), electron back scatter diffraction (EBSD) and transmission electron microscope (TEM). Results display that stress exponent and deformation activation energy are 5.58 and 241.39 kJ.mol(-1) correspondingly, which suggested that dislocation climb is the principal deformation mechanism. The Arrhenius type constitutive equation is established as epsilon (center dot) = 4.09 x 10(16)[sinh(9.922 x 10(-3)sigma)](5.58)exp(-241394/RT). Microstructure evolution can be characterized by Zener-Holomon parameter (Z) which reflects the combining effect of temperature and strain rate on microstructure. At low lnZ (lnZ<36), the 18R-LPSO phase dissolves from continuous network to blocks and high DRX volume (>50 %) is realized by particle-stimulated nucleation and discontinuous dynamic recrystallization. At moderate lnZ (36 <= lnZ<40), a fine and coarse grains bimodal structure is formed at the original grain boundary by continuous dynamic recrystallization resulting in a DRX volume between 10 % and 50 %. At high lnZ (lnZ >= 40), layered 14H-LPSO phase precipitates and inhibits DRX (DRX volume<10 %) by absorbing dislocations. With combination of dissipation coefficient, instability factor and microstructure analysis, 400 degrees C/0.01-0.05 s(-1) and 450 degrees C/0.01 s(-1) are confirmed as optimal hot working domains for the as-cast alloy, under which conditions bimodal microstructure and equiaxed grains microstructure (average grain size 10.3 mu m) can be formed correspondingly.
引用
收藏
页数:15
相关论文
共 50 条
  • [21] Strain-induced heterogeneous bimodal microstructure behavior of Mg-Gd-Y-Zn-Zr alloy containing LPSO phase during hot compression
    Jia, Jingjing
    Zhang, Honglei
    Meng, Mu
    Yang, Xue
    Zhang, Xuhui
    Zhang, Zhimin
    JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2023, 27 : 4264 - 4277
  • [22] Hot Compression Behavior and Microstructure Evolution of an Mg-Gd-Y-Zn-Zr Alloy Containing the 14H LPSO Phase with Different Morphologies
    Han, Yuxiang
    Chen, Zhiyong
    Chen, Han
    Huang, Jingyi
    Liu, Chuming
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2023, 54 (12): : 4806 - 4824
  • [23] Characterization of hot deformation behavior of as-extruded Mg-Gd-Y-Zn-Zr alloy
    Xia, Xiangsheng
    Chen, Qiang
    Li, Jianping
    Shu, Dayu
    Hu, Chuankai
    Huang, Shuhai
    Zhao, Zude
    JOURNAL OF ALLOYS AND COMPOUNDS, 2014, 610 : 203 - 211
  • [24] Effect of Sn microalloying on the hot deformation behavior of Mg-Gd-Y-Zn-Zr alloy
    Zeng, Jian
    Wang, Bing
    Shi, Yuelong
    Zhang, Qian
    Wang, Fulin
    Wang, Fenghua
    Dong, Shuai
    Jin, Li
    Dong, Jie
    JOURNAL OF ALLOYS AND COMPOUNDS, 2025, 1022
  • [25] Hot deformation and dynamic recrystallization behaviors of Mg-Gd-Y-Zr alloy
    Xiao, H. C.
    Jiang, S. N.
    Tang, B.
    Hao, W. H.
    Gao, Y. H.
    Chen, Z. Y.
    Liu, C. M.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2015, 628 : 311 - 318
  • [26] The effect of LPSO phase on hot deformation behavior and dynamic recrystallization evolution of Mg-2.0Zn-0.3Zr-5.8Y alloy
    Lv, Bin-Jiang
    Peng, Jian
    Peng, Yi
    Tang, Ai-Tao
    Pan, Fu-Sheng
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2013, 579 : 209 - 216
  • [27] Hot Compression Behavior of Mg–Gd–Y–Zn–Zr Alloy Containing LPSO with Different Morphologies
    Rui Guo
    Xi Zhao
    Bo-Wen Hu
    Xue-Dong Tian
    Qiang Wang
    Zhi-Min Zhang
    Acta Metallurgica Sinica (English Letters), 2023, 36 : 1680 - 1698
  • [28] Strain dependency of dynamic recrystallization during thermomechanical processing of Mg-Gd-Y-Zn-Zr alloy
    Aalipour, Z.
    Zarei-Hanzaki, A.
    Moshiri, A.
    Abedi, H. R.
    Waryoba, Daudi
    Kisko, A.
    Karjalainen, L. P.
    JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2022, 18 : 591 - 598
  • [29] Hot deformation behavior and microstructural evolutions of a Mg-Gd-Y-Zn-Zr alloy prepared by hot extrusion
    Ling, Zihan
    Yang, Kaipeng
    Wang, Liqing
    Ma, Kai
    Zhang, Dongdong
    Li, Yunlong
    Zhang, Zhen
    Zhao, Zhanyong
    Bai, Peikang
    JOURNAL OF ALLOYS AND COMPOUNDS, 2024, 1009
  • [30] Hot tensile deformation behaviors and a fracture damage model of the Mg-Gd-Y-Zn-Zr alloy
    Yang, Xue
    Zhang, Zhimin
    Meng, Mu
    Jia, Jingjing
    Zhang, Honglei
    Lei, Genxing
    Yu, Jianmin
    JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2022, 18 : 255 - 267