Corrosion behavior of N80 carbon steel in CO2 environments: Investigating the role of flow velocity and silty sand through experimental and computational simulation

被引：1
|
作者：
Li, Hai [1 ]
Liu, Wei [1 ]
Chen, Longjun [1 ]
Zhang, Haoyu [1 ]
Zhang, Bo [1 ]
Sun, Yipu [1 ]
Wang, Fulong [1 ]
Hou, Bowen [1 ]
机构：
[1] Univ Sci & Technol Beijing, Inst Adv Mat & Technol, Corros & Protect Ctr, Beijing 100083, Peoples R China
来源：
CORROSION SCIENCE | 2024年 / 237卷
基金：
中国国家自然科学基金;
关键词：
Flow velocity; Silty sand; Corrosion product layer; Wall shear stress; CO2; corrosion; DIOXIDE CORROSION; EROSION-CORROSION; MECHANISMS;
D O I：
10.1016/j.corsci.2024.112337
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The effects of flow velocity and silty sand on CO2 corrosion of N80 carbon steel were studied using a small flow loop. Silty sand does not change the electrochemical characterization of corrosion but reduces the corrosion rate of steel. Under the low flow velocity, silty sand embeds in the sample surface, reducing active area for iron dissolution and delaying the formation of FeCO3 in corrosion product layer. At medium and high flow velocity, silty sand erodes the sample surface, and wall shear stress damages the integrity of the corrosion product layer, but do not lead to greater corrosion rate.
引用
收藏
页数：16
相关论文
共 50 条
  • [21] Role of polyacrylamide concentration on corrosion behavior of N80 steel in the HPAM/H2S/CO2 environment
    Dong, Baojun
    Zeng, Dezhi
    Yu, Zhiming
    Zhang, Haixin
    Yu, Huiyong
    Tian, Gang
    Yi, Yonggang
    MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2020, 71 (04): : 526 - 536
  • [22] Insight into the role of silty sand in FeCO3 precipitation on carbon steel during CO2 corrosion: Experiments, theoretical simulation and modelling
    Chen, Longjun
    Liu, Wei
    Sun, Yipu
    Li, Hai
    Zhang, Bo
    Wang, Tianguan
    Zhou, Jing
    Hu, Junying
    CORROSION SCIENCE, 2023, 224
  • [23] Joint effect of temperature, stress states and sulfur ions on the CO2 corrosion behavior of N80 tubing steel
    Li, J. B.
    Hou, X.
    Zheng, M. S.
    Zhu, J. W.
    INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE, 2007, 2 (08): : 607 - 617
  • [24] Effect of Flow Rate on the Corrosion Behavior of N80 Steel in Simulated Oil Field Environment Containing CO2 and HAc
    Niu, Qingwei
    Li, Zili
    Cui, Gan
    Wang, Bingying
    INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE, 2017, 12 (11): : 10279 - 10290
  • [25] Investigation on CO2 corrosion Behaviors of N80 tubing steel under stress conditions
    Li Dang-Guo
    Feng Yao-Rong
    Bai Zhen-Quan
    Zhen Mao-Sheng
    ACTA CHIMICA SINICA, 2007, 65 (17) : 1807 - 1813
  • [26] Corrosion inhibition and adsorption behavior of imidazoline salt on N80 carbon steel in CO2-saturated solutions and its synergism with thiourea
    Okafor, P. C.
    Liu, C. B.
    Liu, X.
    Zheng, Y. G.
    Wang, F.
    Liu, C. Y.
    Wang, F.
    JOURNAL OF SOLID STATE ELECTROCHEMISTRY, 2010, 14 (08) : 1367 - 1376
  • [27] Inhibition of CO2 corrosion of N80 carbon steel by carboxylic quaternary imidazoline and halide ions additives
    P. C. Okafor
    C. B. Liu
    X. Liu
    Y. G. Zheng
    Journal of Applied Electrochemistry, 2009, 39 : 2535 - 2543
  • [28] Influence of H2S Content on CO2 Corrosion Behaviors of N80 Tubing Steel
    Jingen, D.
    Wei, Y.
    Xiaorong, L.
    Xiaoqin, D.
    PETROLEUM SCIENCE AND TECHNOLOGY, 2011, 29 (13) : 1387 - 1396
  • [29] Insights into the effect of H2S on the corrosion behavior of N80 steel in supercritical CO2 environment
    Sun, Chong
    Ding, Tiancong
    Sun, Jianbo
    Lin, Xueqiang
    Zhao, Weimin
    Chen, Hui
    JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2023, 26 : 5462 - 5477
  • [30] Effect of Alloying Elements on the Corrosion Behavior of Carbon Steel in CO2 Environments
    Choi, Yoon-Seok
    Nesic, Srdjan
    Jung, Hwan-Gyo
    CORROSION, 2018, 74 (05) : 566 - 576
12345