Enhanced Strength-Ductility Combination in Laser Welding of CrCoNi Medium-Entropy Alloy with Ultrasonic Assistance

The welded joints of high/medium entropy alloys (H/MEAs) have shown sound mechanical properties, indicating high promise for the industrial application of this new type of metal alloy. However, these joints possess either relatively low strength or low ductility. In this paper, we used ultrasonic-assisted laser welding to weld CrCoNi MEA with the nitrogen as shielding gas. The results showed that the tensile strength of the joint at room and cryogenic temperature is 686 MPa and 1071 MPa, respectively. The elongation at room and cryogenic temperature is 26.8% and 27.7%, respectively. The combination of the strength and ductility in our joints exceeds that of other welded H/MEA joints. We attributed this excellent combination to the refined dendrite, the solution of nitrogen into the matrix, and the low stacking fault energy of the CrCoNi MEA. The findings in this paper not only provide a novel way to weld H/MEAs with high strength and ductility, also are useful for additively manufacturing the high-performance component of H/MEAs.