Influence of Zr addition on the microstructure, mechanical and electrical properties of Mo-Cu alloy

被引:1
作者
Zhang, He [1 ,2 ]
Zhang, Guo-Hua [1 ]
机构
[1] Univ Sci & Technol Beijing, State Key Lab Adv Met, Beijing 100083, Peoples R China
[2] Ansteel Beijing Res Inst Co Ltd, Beijing 102209, Peoples R China
来源
MATERIALS TODAY COMMUNICATIONS | 2024年 / 41卷
关键词
Solution strengthening; Grain boundaries; Phase interface; Fine-grain strengthening; Dispersion strengthening; FREEZE-DRYING METHOD; LOW-TEMPERATURE; GRAIN-BOUNDARY; ELEMENTS TI; COMPOSITES; FABRICATION; POWDERS; PARTICLES; STRENGTH; FRACTURE;
D O I
10.1016/j.mtcomm.2024.110307
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
In order to strengthen the overall properties of Mo-Cu alloy, Zr was added to Mo-Cu alloy to enhance the bond strength of Mo/Cu interface and form solid solution strengthening effect. The excellent properties of Mo-Cu-Zr blocks were attained through infiltrating Cu-Zr blocks containing various Zr contents into the Mo skeleton. Compared to the incoherent interface of Mo/Cu in Mo-Cu block, the addition of Zr changed its interface to the coherent interface of Mo-Zr/Cu-Zr. All Mo-Cu-Zr alloy blocks possessed high densification degrees (97.1 %similar to 98.4 %) to assure the excellent general properties. Besides, the formations of Mo-Zr and Cu-Zr solid solutions assured the block owned excellent mechanical strength. Especially, the addition of Zr purified the grain boundary through absorbing oxygen to produce ZrO2 which prevented the Mo-Zr grain growth. As increasing Zr amount from 0 to 4.73 wt%, the Mo-Zr (or Mo) grain size reduced from 5 to 4.0 mu m. Mo-Cu sintered sample containing 2.40 wt% Zr possessed the highest tension strength of 494 MPa. Besides, since the finer grain size of Mo-Zr alloy, this block also owned the highest micro-hardness (250 HV) and bending strength (1626 MPa), respectively. But, the generations of Cu-Zr solid-solution and ZrO2 also damaged the electrical conductivities to a certain extent. Specifically, as the addition amount of zirconium increased from 0 to 2.40 wt%, the conductivity decreased from 42.67 % to 32.15 %IACS.
引用
收藏
页数:11
相关论文
共 54 条
  • [11] Microstructure and high temperature deformation behavior of the Mo-ZrO2 alloys
    Cui, Chaopeng
    Gao, Yimin
    Wei, Shizhong
    Zhang, Guoshang
    Zhou, Yucheng
    Zhu, Xiangwei
    [J]. JOURNAL OF ALLOYS AND COMPOUNDS, 2017, 716 : 321 - 329
  • [12] Das J., 2014, Mater. Sci. Eng., V613
  • [13] Achieving high strength and ductility in ODS-W alloy by employing oxide@W core-shell nanopowder as precursor
    Dong, Zhi
    Ma, Zongqing
    Yu, Liming
    Liu, Yongchang
    [J]. NATURE COMMUNICATIONS, 2021, 12 (01)
  • [14] [都娟 DU Juan], 2007, [北京科技大学学报, Journal of University Science and Technology Beijing], V29, P1010
  • [15] Fan JL, 2008, RARE METAL MAT ENG, V37, P1471
  • [16] Effect of alloying elements Ti, Zr on the property and microstructure of molybdenum
    Fan, Jinglian
    Lu, Mingyuan
    Cheng, Huichao
    Tian, Jiamin
    Huang, Boyun
    [J]. INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS, 2009, 27 (01) : 78 - 82
  • [17] Temperature dependent tensile and fracture behaviors of Mo-10 wt.% Cu composite
    Fang, F.
    Zhou, Y. Y.
    Yang, W.
    [J]. INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS, 2014, 42 : 120 - 125
  • [18] Modeling of the sliding resistance of Σ3⟨111⟩ tungsten grain boundary:: influence of boron additive
    Fuks, D
    Mundim, K
    Liubich, V
    Dorfman, S
    Felsteiner, J
    Borstel, G
    [J]. COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING, 2001, 32 (3-4) : 591 - 594
  • [19] Ge CC, 2000, J UNIV SCI TECHNOL B, V7, P122
  • [20] Characterization of ductile phase toughening mechanisms in a hot-rolled tungsten heavy alloy
    Haag, James, V
    Edwards, Danny J.
    Henager, Charles H., Jr.
    Setyawan, Wahyu
    Wang, Jing
    Murayama, Mitsuhiro
    [J]. ACTA MATERIALIA, 2021, 204