Optimal development and performance evaluation of electrolytic graphene oxide synergistic all-solid waste cementitious grouting material

The low-carbon and friendly alkali-activated cementitious (AACM) grouting material has a broad application potential in the field of grouting engineering due to its excellent workability and higher early strength and is expected to replace cement grouting material in the future. In this study, an AACM grouting material using electrolytic graphene oxide (EGO) synergistic ground granulated blast-furnace slag (GGBS)-fly ash (FA)-rice husk ash (RHA) solid waste was proposed. The optimal ratio was 0.025 % EGO, 8.13 % FA, 26.6 % RHA, and 65.27 % GGBS, which determined by the Analytic Hierarchy Process (AHP), Entropy Weight Method (EWP), and Technique for Order of Preference by Similarity to Ideal Solution (TOPSIS) methods. A systematic evaluation of the mechanical properties and impermeability of the proposed AACM grouting material was conducted by macro experiments (compressive strength, flexural strength and permeability) and micro experiments (XRD, SEM-EDS, Fourier Transform Infrared Spectrometer (FTIR) and Thermogravimetry Analysis (TG)). The results show that the increment of compressive strength and flexural strength for AACM grouting material with 0.025 % EGO compared to the cement water-glass grouting material were 161.2 % and 2.9 %, respectively, at 7-day. While the permeability coefficient compared to AACM grouting material without EGO decreased by 43.9 %. The XRD results show that the EGO reduced the intensity of AACM grouting material diffraction peaks, and FTIR analysis reveals that EGO increased the visibility of O-C-O characteristic peaks. These confirmed that EGO could enhance the degree of alkali activation reaction. The TG results indicate that the addition of EGO promoted the formation of carbonates, which strengthen the mechanical properties of AACM grouting material. The SEM-EDS results demonstrate that EGO increased the Ca/Si ratio, promoted the formation of highly polymerized hydration products.