Study on Microstructure and High-Temperature Mechanical Properties of Al-Mg-Sc-Zr Alloy Processed by LPBF

被引:1
作者
Ren, Zhihao [1 ,2 ]
Zhang, Hao [2 ]
Shu, Xuedao [1 ]
Xu, Haijie [1 ]
Chen, Siyuan [1 ]
Ding, Yaoyao [3 ]
Liang, Liwen [2 ]
Qiu, Zixiang [2 ]
Yang, Yang [2 ]
Zheng, Yongjian [2 ]
机构
[1] Ningbo Univ, Fac Mech Engn & Mech, Ningbo 315211, Peoples R China
[2] Chinese Acad Sci, Ningbo Inst Mat Technol & Engn, Ningbo 315201, Peoples R China
[3] China SciLong Lightweight Technol Co Ltd, Ningbo 315336, Peoples R China
关键词
additive manufacturing; aluminum alloy; microstructure; high-temperature performance; ALUMINUM-ALLOYS; LASER;
D O I
10.3390/met14080890
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Al-Mg-Sc-Zr alloy processed via laser powder bed fusion (LPBF) is poised for significant application in aerospace, where its high-temperature capabilities are paramount for the safety and longevity of engineered structures. This study offers a systematic examination of the alloy's high-temperature tensile properties in relation to its microstructure and precipitate phases, utilizing experimental approaches. The LPBF-processed Al-Mg-Sc-Zr alloy features a bimodal microstructure, with columnar grains in the melt pool's interior and equiaxed grains along its boundary, conferring exceptional properties. The application of well-calibrated processing parameters has yielded an alloy with an impressive relative density of 99.8%, nearly fully dense. Following a thermal treatment of 350 degrees C for 4 h, the specimens were subjected to tensile tests at both room and elevated temperatures. The data reveal that the specimens exhibit a tensile strength of 560.6 MPa and an elongation of 11.1% at room temperature. A predictable decline in tensile strength with rising temperature is observed: at 100 degrees C, 150 degrees C, 200 degrees C, and 250 degrees C; the respective strengths and elongations are 435.1 MPa and 25.8%, 269.4 MPa and 20.1%, 102.8 MPa and 47.9%, 54.0 MPa and 72.2%. These findings underpin the technical rationale for employing LPBF-processed Al-Mg-Sc-Zr alloy in aerospace applications.
引用
收藏
页数:15
相关论文
共 42 条
[1]   APPLICATION OF FRACTURE MECHANICS TO ALUMINUM-ALLOYS SELECTION [J].
BATHIAS, C .
ENGINEERING FRACTURE MECHANICS, 1978, 10 (02) :267-282
[2]   Intensive processing optimization for achieving strong and ductile Al-Mn-Mg-Sc-Zr alloy produced by selective laser melting [J].
Bayoumy, D. ;
Schliephake, D. ;
Dietrich, S. ;
Wu, X. H. ;
Zhu, Y. M. ;
Huang, A. J. .
MATERIALS & DESIGN, 2021, 198
[3]   Grain refinement of laser remelted Al-7Si and 6061 aluminium alloys with Tibor® and scandium additions [J].
Carluccio, D. ;
Bermingham, M. J. ;
Zhang, Y. ;
StJohn, D. H. ;
Yang, K. ;
Rometsch, P. A. ;
Wu, X. ;
Dargusch, M. S. .
JOURNAL OF MANUFACTURING PROCESSES, 2018, 35 :715-720
[4]   Development of fatigue cracks from mechanically machined scratches on 2024-T351 aluminium alloy-part I: experimentation and fractographic analysis [J].
Cini, A. ;
Irving, P. E. .
FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2017, 40 (05) :776-789
[5]   Effects of powder reuse on the microstructure and mechanical behaviour of Al-Mg-Sc-Zr alloy processed by laser powder bed fusion (LPBF) [J].
Cordova, Laura ;
Bor, Ton ;
de Smit, Marc ;
Carmignato, Simone ;
Campos, Monica ;
Tinga, Tiedo .
ADDITIVE MANUFACTURING, 2020, 36
[6]   Effects of Sc and Zr on mechanical property and microstructure of tungsten inert gas and friction stir welded aerospace high strength Al-Zn-Mg alloys [J].
Deng, Ying ;
Peng, Bing ;
Xu, Guofu ;
Pan, Qinglin ;
Yin, Zhimin ;
Ye, Rui ;
Wang, Yingjun ;
Lu, Liying .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2015, 639 :500-513
[7]   Design, microstructure and thermal stability of a novel heat-resistant Al-Fe-Ni alloy manufactured by selective laser melting [J].
Ding, Han ;
Xiao, Yakai ;
Bian, Zeyu ;
Wu, Yi ;
Yang, Huihui ;
Wang, Hongze ;
Wang, Haowei .
JOURNAL OF ALLOYS AND COMPOUNDS, 2021, 885
[8]   Excellent strength–ductility balance of Sc-Zr-modified Al–Mg alloy by tuning bimodal microstructure via hatch spacing in laser powder bed fusion [J].
Ekubaru Y. ;
Gokcekaya O. ;
Ishimoto T. ;
Sato K. ;
Manabe K. ;
Wang P. ;
Nakano T. .
Materials and Design, 2022, 221
[9]   Hall-Petch relation and boundary strengthening [J].
Hansen, N .
SCRIPTA MATERIALIA, 2004, 51 (08) :801-806
[10]  
Jgle E.A., 2016, DARE ANN WORKSH 2016