High-temperature tribological behavior of the Al/Mg/Cu multilayered composite produced by the severe plastic deformation

被引:2
作者
Shi, Xiaoling [1 ]
Wang, Xiangling [1 ]
Zhang, Jiaming [1 ]
Du, Huiqi [1 ]
机构
[1] Lyuliang Univ, Dept Resources & Mech Engn, Lvliang, Peoples R China
关键词
Laminated composite; Al/Mg/Cu; Hot wear behavior; ARB; MECHANICAL-PROPERTIES; WEAR BEHAVIOR; MICROSTRUCTURE; STRENGTH; INTERFACE;
D O I
10.1016/j.triboint.2024.110037
中图分类号
TH [机械、仪表工业];
学科分类号
0802 ;
摘要
In the current research, the microstructure and wear behavior of Al/Mg/Cu multilayered composite at high temperatures were investigated. For this purpose, the Al/Mg/Cu composite was produced by the accumulative roll bonding (ARB) process and continued until the sixth pass at ambient temperature. The hot wear tests were performed at loads of 10, 20, and 40 N at 100, 150, and 250 degrees C for different passes. The findings demonstrated that with the increase of ARB passes, the wear rate decreased. So under 40 N at 100, 150, and 250 degrees C, the wear rate in the sixth pass decreased by 53 %, 65 %, and 76 %, respectively, compared to the first pass. The examination of the worn surfaces showed at 100 degrees C under high loads, fatigue wear was dominant. At 150 degrees C, oxidation was the main wear mechanism. The presence of oxidized grooves on the surface showed that the abrasive wear encouraged oxidation. At 250 degrees C under 40 N, inhomogeneous oxidation was the main wear mechanism of the samples. So that aluminum and magnesium regions were oxidized and copper areas remained un-oxidized like isolated islands.
引用
收藏
页数:16
相关论文
共 84 条
  • [41] Effects of fretting wear process on fatigue crack propagation and life assessment
    Pinto, A. L.
    Araujo, J. A.
    Talemi, R.
    [J]. TRIBOLOGY INTERNATIONAL, 2021, 156
  • [42] Influence of GNPs solid lubricant on the fabrication of Cu/SS304L composite micro channels
    Ren, Mengyuan
    Xie, Haibo
    Lin, Fei
    Wu, Hui
    Yuan, Shengnan
    Li, Zhou
    Yang, Ming
    Manabe, Ken-ichi
    Jiang, Zhengyi
    [J]. TRIBOLOGY INTERNATIONAL, 2024, 194
  • [43] PLASTIC-DEFORMATION AND SLIDING FRICTION OF METALS
    RIGNEY, DA
    HIRTH, JP
    [J]. WEAR, 1979, 53 (02) : 345 - 370
  • [44] On the impact of using alumina nanoparticles and initial aging on the microstructure and mechanical properties of the AA1050/AA2024 nanostructure composite, created by accumulative roll bonding (ARB) method
    Roghani, Hamed
    Borhani, Ehsan
    Jafarian, Hamid Reza
    Yousefieh, Mohammad
    Naseri, Majid
    Moghadam, Ahmad Ostovari
    [J]. WEAR, 2023, 526
  • [45] Comprehensive investigation on wear and microstructure development in Al/ti ultrafine grained multi-layered composite produced by Accumulative Roll Bonding (ARB)
    Sadeghinia, H.
    Jafarian, H. R.
    Salehi, M. T.
    Eivani, A. R.
    [J]. MATERIALS RESEARCH EXPRESS, 2019, 6 (11)
  • [46] Strength prediction of multi-layered copper-based composites fabricated by accumulative roll bonding
    Seifollahzadeh, P.
    Alizadeh, Morteza
    Abbasi, M. R.
    [J]. TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2021, 31 (06) : 1729 - 1739
  • [47] Dry sliding wear behavior of open-cell Al-Mg/Al2O3 and Al-Mg/SiC-Al2O3 composite preforms produced by a pressureless infiltration technique
    Sharifi, Hassan
    Ostovan, Kianoush
    Tayebi, Morteza
    Rajaee, Ali
    [J]. TRIBOLOGY INTERNATIONAL, 2017, 116 : 244 - 255
  • [48] Effects of fretting wear on rolling contact fatigue
    Sharma, Akshat
    Sadeghi, Farshid
    [J]. TRIBOLOGY INTERNATIONAL, 2024, 192
  • [49] Sheu S., 2013, Tribology in Hot Rolling of Metal BT - Encyclopedia of Tribology, P3830, DOI [10.1007/978-0-387-92897-5622, DOI 10.1007/978-0-387-92897-5622]
  • [50] Contact cracking and delamination of thin solid lubricating films on deformable substrates
    Shu, Kun
    Zhang, Chuanwei
    Sun, Dong
    Wu, Bo
    Li, Zhen
    Wu, Jiqiang
    Zheng, Dezhi
    Gu, Le
    [J]. TRIBOLOGY INTERNATIONAL, 2021, 163