Controlled Amphiphilicity and Thermo-Responsiveness of Functional Copolymers Based on Oligo(Ethylene Glycol) Methyl Ether Methacrylates

In this work, comb homopolymers as well as comb-type copolymers of thermo-responsive oligo(ethylene glycol methyl ether methacrylate)s, OEGMAs, with various chain lengths (DEGMA, PEGMA500, and PEGMA950 containing 2, 9, or 19 repeating ethylene glycol units, respectively) were synthesized through free radical (co)polymerization. For the copolymers, either the functional hydrophobic glycidyl methacrylate (GMA) or the inert hydrophilic N,N-dimethylacrylamide (DMAM) were selected as comonomers. The self-assembly and thermo-responsive behavior of the products was investigated through Nile Red fluorescence probing, turbidimetry, and dynamic light scattering (DLS). Interestingly, it was found that all OEGMA-based homopolymers exhibit a tendency to self-organize in aqueous media, in addition to thermo-responsiveness. The critical aggregation concentration (CAC) increases with the number of repeating ethylene oxide units in the OEGMA macromonomers (CAC was found to be 0.003, 0.01, and 0.03% w/v for the homopolymers PDEGMA, PPEGMA500, and PPEGMA950, respectively). Moreover, the CAC of the copolymers in aqueous media is highly affected by the incorporation of hydrophobic GMA or hydrophilic DMAM units, leading to lower or higher values, respectively. Thus, the CAC decreases down to 0.003% w/v for the GMA-richest copolymer of PEGMA950, whereas CAC increases up to 0.01% w/v for the DMAM-richest copolymer of DEGMA. Turbidimetry and DLS studies proved that the thermo-sensitivity of the polymers is governed by several parameters such as the number of repeating ethylene glycol groups in the side chains of the OEGMAs, the molar percentage of the hydrophobic or hydrophilic comonomers, along with the addition of salts in the aqueous polymer solutions. Thus, the cloud point of the homopolymer PDEGMA was found at 23 degrees C and it increases to 33.5 degrees C for the DMAM-richest copolymer of DEGMA. Lastly, the formation of a hydrogel upon heating aqueous mixtures of the GMA-comprising copolymers with silica nanoparticles overnight is strong evidence of the functional character of these polymers.