High-cycle fatigue behavior of IN 738LC superalloy at high temperatures

被引：1

作者：

Hornik, Vit ^{[1
,2
]}

Baca, Adrian ^{[1
]}

Smid, Miroslav ^{[1
]}

Hrbacek, Karel ^{[3
]}

Hutar, Pavel ^{[1
,2
]}

机构：

[1] AS CR, Inst Phys Mat, Zizkova 22, Brno 61662, Czech Republic

[2] CEITEC IPM, Zizkova 22, Brno 61662, Czech Republic

[3] PBS Velka Bites AS, Vlkovska 279, Velka Bites 59512, Czech Republic

来源：

10TH INTERNATIONAL CONFERENCE ON MATERIALS STRUCTURE AND MICROMECHANICS OF FRACTURE, MSMF | 2023年 / 43卷

关键词：

high-cycle fatigue; superalloy; high-temperatures; IN; 738LC; fractography;

D O I：

10.1016/j.prostr.2022.12.248

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

The presented study is focused on experimental results of high-cycle fatigue life of a cast polycrystalline nickel-based superalloy IN 738LC at temperatures of 800, 900, and 950 degrees C. The absence of hot isostatic pressing (HIP) led to the occurrence of casting defects in the microstructure. The fatigue tests were performed in symmetrical loading in laboratory air. The fracture surfaces of specimens were studied by scanning electron microscopy to describe the influence of temperature on the fatigue damage mechanism and fatigue crack initiation. Change in the primary crack propagation mechanism from crystalline (stage I regime) to non-crystalline (stage II regime) mechanism was observed with increasing temperature. However, the effect of changing mechanism caused by temperature dependence was unfavorably influenced by casting defects. (c) 2023 The Authors. Published by Elsevier B.V.

引用

页码：136 / 141

页数：6

共 8 条

[1] Casting defects and high temperature fatigue life of IN 713LC superalloy [J].

Kunz, Ludvik ;

Lukas, Petr ;

Konecna, Radomila ;

Fintova, Stanislava .

INTERNATIONAL JOURNAL OF FATIGUE, 2012, 41 :47-51

[2] Fatigue behaviour and lifing of two single crystal superalloys [J].

MacLachlan, DW ;

Knowles, DM .

FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2001, 24 (08) :503-521

[3] High temperature fatigue of nickel-base superalloys - A review with special emphasis on deformation modes and oxidation [J].

Pineau, Andre ;

Antolovich, Stephen D. .

ENGINEERING FAILURE ANALYSIS, 2009, 16 (08) :2668-2697

[4] Nickel-based superalloys for advanced turbine engines: Chemistry, microstructure, and properties [J].

Pollock, TM ;

Tin, S .

JOURNAL OF PROPULSION AND POWER, 2006, 22 (02) :361-374

[5]

Reed R.C., 2008, The Superalloys: Fundamentals and Applications, DOI DOI 10.1016/j.msea.2004.01.108

[6] High Cycle Fatigue Damage Mechanisms of MAR-M 247 Superalloy at High Temperatures [J].

Smid, M. ;

Hornik, V. ;

Hutar, P. ;

Hrbacek, K. ;

Kunz, L. .

TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 2016, 69 (02) :393-397

[7] High Cycle Fatigue Data Transferability of MAR-M 247 Superalloy from Separately Cast Specimens to Real Gas Turbine Blade [J].

Smid, Miroslav ;

Hornik, Vit ;

Kunz, Ludvik ;

Hrbacek, Karel ;

Hutar, Pavel .

METALS, 2020, 10 (11) :1-16

[8] Stage I fatigue cracking in MAR-M 247 superalloy at elevated temperatures [J].

Smid, Miroslav ;

Hutar, Pavel ;

Hornik, Vit ;

Hrbacek, Karel ;

Kunz, Ludvik .

21ST EUROPEAN CONFERENCE ON FRACTURE, (ECF21), 2016, 2 :3018-3025

← 1 →